A method of desulfurizing steel including steps of forming a slag over a molten metal, drawing a vacuum to less than 5 torr over the slag and molten metal, stirring the molten metal and slag, and deoxidizing and desulfurizing the molten metal and slag to degas the steel reducing at least sulfur, nitrogen, oxygen, and hydrogen contents, and reducing activity of oxygen in the molten metal to less than 30 ppm. The method includes forming a slag composition after degassing the steel comprising CaO between about 50 and 70% by weight, SiO2 between about 20 and 28% by weight, CaF2 between about 5 and 15% by weight, MgO not more than 8% by weight, Al2O3 not more than 1% by weight, and a combination of FeO+MnO not more than 2% by weight, where the sum of CaO+CaF2+SiO2+MgO is at least 85% by weight.