Provided is material for an aluminum alloy exhibiting a sufficient heat resistance, tensile strength as well as stress corrosion cracking resistance necessary for use as automobile parts. Also, provided are a forged part forged from such aluminum alloy and an aluminum alloy high strength bolt made thereof. The aluminum alloy (by mass) is consisted of (by mass) 1.0 to 1.7% of Si, 0.05 to 0.5% of Fe, 0.8 to 1.5% of Cu, 0.6 to 1.2% of Mn, 0.9 to 1.5% of Mg, 0.05 to 0.5% of Zn, 0.05 to 0.3% of Zr, 0.01 to 0.2% of V, and when needed, Ti exceeding 0% and not more than 0.05%, and, when further needed, Ni exceeding 0% and not more than 0.7%, the remainder being Al and unavoidable impurities.