An anode active material for use in a lithium secondary battery including a mixture of graphite I that has, according to X-ray powder diffraction, d002 of not smaller than 0.3354 nm and not greater than 0.337 nm, Lc(004) of smaller than 100 nm, La(110) of not smaller than 100 nm, and a half width of the peak of a plane (101) at a diffraction angle (2θ) of 44 degrees to 45 degrees of not smaller than 0.65 degree and another graphite so as to have, according to X-ray powder diffraction, d002 of not smaller than 0.3354 nm and not greater than 0.337 nm, Lc(004) of not smaller than 80 nm, La(110) of not smaller than 100 nm, and a half width of the peak of a plane (101) at a diffraction angle (2θ) of 44 degrees to 45 degrees of not smaller than 0.5 degree.