The present invention provides a bake-hardenable high-strength cold-rolled steel sheet having excellent bake hardenability, cold aging resistance, and deep-drawability, and reduced planar anisotropy, containing chemical components in % by mass of: C: 0.0010% to 0.0040%, Si: 0.005% to 0.05%, Mn: 0.1% to 0.8%, P: 0.01% to 0.07%, S: 0.001% to 0.01%, Al: 0.01% to 0.08%, N: 0.0010% to 0.0050%, Nb: 0.002% to 0.020%, and Mo: 0.005% to 0.050%, a value of [Mn %]/[P %] being in the range of 1.6 to 45, where [Mn %] is an amount of Mn and [P %] is an amount of P, an amount of C in solid solution obtained from [C %]−(12/93)×[Nb %] being in the range of 0.0005% to 0.0025%, where [C %] is an amount of C and [Nb %] is an amount of Nb, with a balance including Fe and inevitable impurities, wherein the bake-hardenable high-strength cold-rolled steel sheet satisfies the following Equation (1), where X(222), X(110), and X(200) represent ratios of integrated intensity of X-ray diffraction of {222} plane, {110} plane, and {200} plane, respectively, being parallel to a plane located at a depth of ¼ plate thickness measured from the surface of the steel sheet, and the bake-hardenable high-strength cold-rolled steel sheet has tensile strength in the range of 300 MPa to 450 MPa.