A BÏ2212 article may be formed by mixing metallic precursor powders including bismuth, strontium, calcium and copper in an oxygen-free atmosphere, mechanically alloying the metallic precursor powders in an oxygen-free atmosphere, and heating the metallic precursor alloy according to a temperature profile. The profile may include a ramp-up stage during which the alloy is heated to a peak temperature in an oxygen-free atmosphere, a dwell stage during which the alloy is held at the peak temperature for a dwell time, and a ramp-down stage during which the alloy is cooled from the peak temperature. During at least a portion of the dwell stage, the oxygen-free atmosphere is switched to an oxygen-inclusive atmosphere, wherein the alloy is oxidized to form a superconducting oxide, which may be sintered during or after oxidation. The alloy may be formed into a shape, such as a wire, prior to oxidizing.