摘要:
The present invention relates to a multi-layer oriented shrink film comprising at least one skin layer comprising a polystyrene material and at least one core layer comprising a polyolefin layer. The films are preferably primarily oriented in either the machine or the cross direction. These films are ideally suited for use as a shrink label which can be applied either as a CD shrink sleeve or applied using a continuous roll process. The films ideally have an overall density of less than 1.0 g/cm3, to facilitate recycling efforts.
摘要翻译:本发明涉及一种多层定向收缩膜,其包含至少一层包含聚苯乙烯材料的表皮层和至少一层包含聚烯烃层的芯层。 膜优选主要在机器或横向方向上定向。 这些膜理想地适合用作收缩标签,其可以作为CD收缩套筒使用,或者使用连续辊式方法施加。 这些膜理想地具有小于1.0g / cm 3的总密度,以便于再循环。
摘要:
The present invention relates to a multi-layer oriented shrink film comprising at least one skin layer comprising a polystyrene material and at least one core layer comprising a polyolefin layer. The films are preferably primarily oriented in either the machine or the cross direction. These films are ideally suited for use as a shrink label which can be applied either as a CD shrink sleeve or applied using a continuous roll process. The films ideally have an overall density of less than 1.0 g/cm3, to facilitate recycling efforts.
摘要翻译:本发明涉及一种多层定向收缩膜,其包含至少一层包含聚苯乙烯材料的表皮层和至少一层包含聚烯烃层的芯层。 膜优选主要在机器或横向方向上定向。 这些膜理想地适合用作收缩标签,其可以作为CD收缩套筒使用,或者使用连续辊式方法施加。 这些膜理想地具有小于1.0g / cm 3的总密度,以便于再循环。
摘要:
A method of manufacturing a multilayer heat-shrinkable, puncture-resistant biaxially oriented film is disclosed. The method includes a double bubble orientation step and extruding a primary tube that includes at least one substantially linear ethylene homopolymer or interpolymer, wherein the substantially linear ethylene homopolymer or interpolymer has an uniform branching distribution, a melt flow ratio, I.sub.10 /I.sub.2,.gtoreq.5.63, and a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)-4.63, and is also characterized as having essentially no linear polymer fraction, a single DSC melting peak, a density greater than about 0.85 g/cc, and a favorable gas extrusion critical shear rate at the onset of surface melt fracture.
摘要:
The present invention relates to a fiber produced form a composition comprising at least one hydrogenated block copolymer and, optionally, at least one other polymer selected from the group consisting of a reactive tailored liquid polyurethane, an elastomeric or sulfonated ethylene/vinyl aromatic interpolymer, an elastomeric ethylene/C3-C20 &agr;-olefin interpolymer, an C3-C20 &agr;-olefin/conjugated diene interpolymer, an elastic polypropylene polymer, an enhanced polypropylene polymer, an elastomeric thermoplastic polyurethane, an elastic copolyester, a partially hydrogenated block copolymer, an elastic polyamide, a hydroxyl functionalized polyether (or polyetheramine), a styrene/conjugated diene interpolymer, and an elastomeric metallocene-catalyzed synthetic polymer or a blend or formulated system thereof.
摘要翻译:本发明涉及由包含至少一种氢化嵌段共聚物和任选的至少一种其它聚合物制备的纤维,所述其它聚合物选自反应性定制的液体聚氨酯,弹性体或磺化乙烯/乙烯基芳族互聚物, 弹性体乙烯/ C 3 -C 20α-烯烃互聚物,C 3 -C 20α-烯烃/共轭二烯互聚物,弹性聚丙烯聚合物,增强聚丙烯聚合物,弹性体热塑性聚氨酯,弹性共聚酯,部分氢化嵌段共聚物,弹性体 聚酰胺,羟基官能化聚醚(或聚醚胺),苯乙烯/共轭二烯互聚物和弹性体茂金属催化的合成聚合物或其共混物或配制体系。
摘要:
Polymer mixtures are disclosed which comprise at least one homogeneously branched ethylene polymer (A) and at least one ethylene polymer (B) having a crystallinity which is at least 7% greater than the crystallinity of polymer (A) with certain provisos. A process for making a molded article using the disclosed polymer mixtures is disclosed as well as films, film layers, coatings and molded articles formed from those mixtures. These mixtures have several advantages over polymer compositions of the prior art, including improved properties at elevated temperatures such as improved softening point under load, improved hardness, improved toughness, improved 100% modulus of elasticity, improved compression set, improved ability to prevent oil bleed out at lower temperatures when the mixture contains oil and reduced injection molding cycle time. The mixtures retain their performance advantages even when substantial amounts of additives such as oil and filler are incorporated into the mixture. The mixtures may also be crosslinked after they are formed into the shape of an article to form vulcanized elastomeric products. The polymer mixtures have utility in a variety of applications.
摘要:
The present invention relates to a method for making a heat-resistant elastic article and a heat-resistant elastic article. The invention especially relates to a method of making elastic fibers and polymeric elastic fibers wherein the elastic fibers are capable of withstanding dyeing and heat-setting processes that typically are conducted at elevated temperatures (such as 110-230° C. and especially at greater than or equal to 130° C. for minutes). The inventive method comprises radiation crosslinking an article (or plurality of articles) under an inert or oxygen limited atmosphere (for example, in N2, argon, helium, carbon dioxide, xenon and/or a vacuum) wherein the article (or articles) comprises at least one amine stabilizer and preferably another optional stabilizer additive. More preferably, the radiation crosslinking is performed at a low temperature (−50 to 40° C.). The elastic article (or articles) comprises a homogeneously branched ethylene interpolymer (preferably a substantially linear ethylene interpolymer), a substantially hydrogenated block polymer, or a combination of the two. The heat-resistant elastic articles (especially fibers) are useful in various durable or repeated-use fabric applications such as, but not limited to, clothing, under-garments, and sports apparel. The heat-resistant elastic fibers can be conveniently formed into fabrics using well-known techniques such as, for example, by using co-knitting techniques with cotton, nylon, and/or polyester fibers.
摘要:
The present invention relates to a method for making a heat-resistant elastic article and a heat-resistant elastic article. The invention especially relates to a method of making elastic fibers and polymeric elastic fibers wherein the elastic fibers are capable of withstanding dyeing and heat-setting processes that typically are conducted at elevated temperatures (such as 110-230° C. and especially at greater than or equal to 130° C. for minutes). The inventive method comprises radiation crosslinking an article (or plurality of articles) under an inert or oxygen limited atmosphere (for example, in N2, argon, helium, carbon dioxide, xenon and/or a vacuum) wherein the article (or articles) comprises at least one amine stabilizer and preferably another optional stabilizer additive. More preferably, the radiation crosslinking is performed at a low temperature (−50 to 40° C.). The elastic article (or articles) comprises a homogeneously branched ethylene interpolymer (preferably a substantially linear ethylene interpolymer), a substantially hydrogenated block polymer, or a combination of the two. The heat-resistant elastic articles (especially fibers) are useful in various durable or repeated-use fabric applications such as, but not limited to, clothing, under-garments, and sports apparel. The heat-resistant elastic fibers can be conveniently formed into fabrics using well-known techniques such as, for example, by using co-knitting techniques with cotton, nylon, and/or polyester fibers.
摘要:
A method of manufacturing a monolayer heat-shrinkable, puncture-resistant biaxially oriented film is disclosed. The method includes a double bubble orientation step and extruding a primary tube that includes at least one substantially linear ethylene homopolymer or interpolymer, wherein the substantially linear ethylene homopolymer or interpolymer has an uniform branching distribution, a melt flow ratio I.sub.10 /I.sub.2, .gtoreq.5.63, and a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation M.sub.w /M.sub.n .ltoreq.(I.sub.10 /I.sub.2)-4.63, and is also characterized as having essentially no linear polymer fraction, a single DSC melting peak, a density greater than about 0.85 g/cc, and a favorable gas extrusion critical shear rate at the onset of surface melt fracture.
摘要:
Biaxially oriented, heat-shrinkable film-making process and film with improved toughness and extrusion processibility are disclosed. The improved film comprises at least one layer of at least one substantially linear ethylene homopolymer or interpolymer, wherein the substantially linear ethylene polymer has an uniform branching distribution, and is also characterized as having essentially no linear polymer fraction, a single DSC melting peak, a density greater than about 0.85 g/cc, and a simple bubble film 1% secant modulus below 195,000 kPa. The biaxially oriented film is characterized as having a simple bubble shrinkage value of from about 18% to about 85% at 135.degree. C. and is useful in preparing heat-shrink bags for packaging food articles like poultry and fresh red meat.
摘要:
An electronic device module comprising: A. At least one electronic device, e.g., a solar cell, and B. A polymeric material in intimate contact with at least one surface of the electronic device, the polymeric material comprising (1) a polyolefin copolymer characterized as having has an average Mv and a valley temperature between the interpolymer and high crystalline fraction, Thc, such that the average Mv for a fraction above Thc from ATREF divided by average Mv of the whole polymer from ATREF (Mhc/Mp) is less than about 1.95 and wherein the copolymer has a CDBI of less than 60%, (2) optionally, a vinyl silane, (3) optionally, free radical initiator or a photoinitiator in an amount of at least about 0.05 wt % based on the weight of the copolymer, and (4) optionally, a co-agent in an amount of at least about 0.05 wt % based upon the weight of the copolymer.