摘要:
To obtain a water-resistant polarizing film free from deterioration in dichroic ratio caused by water-resistant treatment, it is critical that adjacent sulfonic acid groups or sulfonate groups in the organic dyes to be used for the polarizing film are spaced at moderate intervals. In a process for producing a water-resistant polarizing film of the present invention, the polarizing film before water-resistant treatment includes an organic dye which comprises an azo compound 20 represented by the following general formula (1) or (2)
摘要:
There is provided a method for producing a polarizing film having far superior water resistance to conventional polarizing films by contacting a liquid containing cationic polymers with a surface of a polarizing film.
摘要:
To obtain a water-resistant polarizing film free from deterioration in dichroic ratio caused by water-resistant treatment, it is critical that adjacent sulfonic acid groups or sulfonate groups in the organic dyes to be used for the polarizing film are spaced at moderate intervals. In a process for producing a water-resistant polarizing film of the present invention, the polarizing film before water-resistant treatment includes an organic dye which comprises an azo compound 20 represented by the following general formula (1) or (2)
摘要:
There is provided a method for producing a polarizing film having far superior water resistance to conventional polarizing films by contacting a liquid containing cationic polymers with a surface of a polarizing film.
摘要:
The present invention provides a birefringent film that hardly generates cracks even when the film is exposed under a high-temperature and high-humidity environment for a long period of time. The birefringent film of the present invention is a film containing, as a major component, a lyotropic liquid crystalline polycyclic compound containing an acenaphtho[1,2-b]quinoxaline derivative unit in a molecular structure and having a molecular weight of 500 or higher. The birefringent film of the present invention preferably has a refractive index ellipsoid showing a relationship of nx≧nz>ny, and more preferably has an in-plane birefringence of 0.01 or higher at the wavelength of 590 nm.