摘要:
A method for recovering a crystalline poly(arylene sulfide) from a slurry comprising a particulate poly(arylene sulfide), a polar organic compound, and water, said method comprising:(a) substantially liquefying said particulate poly(arylene sulfide) to form a liquid mixture comprising said substantially liquified poly(arylene sulfide) and said polar organic compound;(b) contacting said liquid mixture with a vaporized separation agent in an amount sufficient to effect a separation between said poly(arylene sulfide) and said polar organic compound;(c) reducing the temperature of said liquid mixture sufficiently to solidify said substantially liquified poly(arylene sulfide) to form a slurry comprising a particulate poly(arylene sulfide); and(d) recovering said particulate poly(arylene sulfide) from said slurry.
摘要:
A method is provided for recovering poly(arylene sulfide) from a liquid reaction mixture, comprising a liquid-phase poly(arylene sulfide) and a polar organic compound which can also function as a solvent for the polymer, and water. The liquid reaction mixture is contacted by an amount of a vaporized phase separation agent at least sufficient to effect or enhance a phase separation of the liquid-phase poly(arylene sulfide) component from the polar organic compound. The poly(arylene sulfide resins recovered according to this invention exhibit greater particle size than those recovered according to prior art methods, and do not tend to adhere to vessel walls during recovery.
摘要:
Phenol is extracted with a chlorinated aromatic extractant, such as p-dichlorobenzene, from an aqueous mixture containing phenol and N-methylpyrrolidone. In an embodiment of this invention the purified N-methylpyrrolidone is recycled for use in a poly(phenylene sulfide) polymerization process.
摘要:
The invention is a process to provide more granular, higher bulk density particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins having associated therewith improved handling.The process for treating a first slurry comprising a solid particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resin dispersed in a liquid medium comprising a polar organic compound, comprises: (a) liquifying the first solid particulate resin in the first slurry to form a first mixture comprising a liquified resin and the polar organic compound; (b) adding, to the first mixture, a sufficient amount of at least one separaton agent to produce a second mixture, and (c) reducing the temperature of the second mixture sufficiently to solidify the liquified resin to form a second slurry comprising a polar organic compound and a second solid particulate resin having a bulk density greater than the first solid particulate resin would if recovered.In other embodiments, the above-described process is accomplished without generating pressure significantly greater than those generated during polymerization reactions of particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins.
摘要:
In one embodiment, the inventive process comprises: (a) preparing a first slurry comprising a first particulate PAS resin and a polar organic compound, (b) heating the first slurry to a temperature in the range of about 20.degree. C. (68.degree. F.) to about 40.degree. C. (104.degree. F.) below the liquid-to-solid phase transitional temperature of the first particulate resin, and (c) rapidly cooling the first slurry to below about 50.degree. C. (122.degree. F.) below the liquid-to-solid phase transitional temperature of the first particulate resin in the polar organic compound to form a second slurry, comprising the polar organic compound and a polymeric mixture comprising a novel particulate high molecular weight PAS resin and a minor amount of a particulate low molecular weight PAS resin.In another embodiment, the inventive process comprises: (a) preparing a liquid mixture comprising a first particulate PAS resin and a polar organic compound, at a temperature above the solid-to-liquid phase transitional temperature of the first particulate resin, (b) slowly cooling the liquid mixture to between about 20.degree. C. (68.degree. F.) to about 40.degree. C. (104.degree. F.) below the liquid-to-solid phase transitional temperature of the first particulate PAS in the polar organic compound resin to form a first slurry comprising the polar organic compound and a second particulate PAS resin, and (c) rapidly cooling the first slurry to about 50.degree. C. (122.degree. F.) below the liquid-to-solid phase transitional temperature of the first particulate resin in the polar organic compound, thus forming a second slurry comprising the polar organic compound and a polymeric mixture comprising a third particulate high molecular weight resin, wherein third particulate resin, when recovered has a higher molecular weight than its respective first and second particulate resins, if recovered by conventional means.
摘要:
A process is provided for preparing more granular (i.e., higher bulk density) particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins having associated therewith improved processability and thermal stability, without generating pressures significantly greater than those generated during polymerization reactions of particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins.
摘要:
In one embodiment, a process is provided for treating virgin arylene sulfide resins, wherein a heated polymer slurry, comprising a virgin arylene sulfide resin and water, is contacted by a buffer solution having a pH less than about 9.35 but greater than that necessary to result in at least a partial curing of the virgin arylene sulfide resin. In a further embodiment, a process is provided for treating a virgin arylene sulfide resin, wherein a virgin arylene sulfide resin is slurried in a buffer solution having a pH less than about 9.35 but greater than that necessary to result in at least a partial curing of the virgin arylene sulfide resin. The treating process of this invention is conducted at an elevated temperature, below the melting point of the virgin arylene sulfide resin, while in the substantial absence of a gaseous oxidizing atmosphere. The treated arylene sulfide resins are recovered from the polymer slurry in a manner which does not result in at least a partial curing of the treated resin.
摘要:
A process is provided for preparing more granular (i.e., higher bulk density) particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins having associated therewith improved processability and thermal stability, without generating pressures significantly greater than those generated during polymerization reactions of particulate poly(arylene sulfide ketone) or poly(arylene sulfide diketone) resins.
摘要:
A process for preparing poly(arylene sulfide sulfone) by contacting a dihaloaromatic sulfone, an organic amide, a sulfur-containing compound, water, and an alkali metal carboxylate, wherein the molar ratio of the alkali metal carboxylate to the sulfur-containing compound is about 0.002:1 to less than 0.05:1.
摘要:
A method of making a poly(arylene sulfide/sulfone) resin comprises heating amorphous poly(arylene sulfide/sulfone) resin at an elevated temperature but below the melting temperature of the resin in a vacuum environment so that extrudate made from the resin is smooth and has reduced gas bubble content. The invention also relates to poly(arylene sulfide/sulfone) resin made in accordance with the method.