摘要:
An ethylene terpolymer wax comprising from 40 to 95% by weight of units of ethylene, from 0.1 to 40% by weight of units of at least one anhydride of a C4-C10-dicarboxylic acid having at least one ethylenic C—C double bond, and from 0.1 to 40% by weight of units of at least one ester of the formula I where R1 is selected from hydrogen, C1-C10-alkyl, C3-C12-cycloalkyl or C6-C14-aryl and R2 is selected from C1-C10-alkyl, C3-C12-cycloalkyl or C6-C14-aryl, having a molecular weight Mw of up to 20000 g/mol.
摘要:
Copolymers of ethylene have from 1 to 30 mol % of alkyl(meth)acrylates and, if desired, other comonomers, and have a residual comonomer content of less than 0.5% by weight in the copolymer. A process for preparing copolymers of this type in a combination of stirred autoclave and tubular reactor is described, as is the use of the copolymers for preparing polyamide molding compositions.
摘要:
A process for coating a reactor, which comprises depositing a metal layer or a metal/polymer dispersion layer on the internal surface of the reactor in an electroless manner by bringing the surfaces into contact with a metal electrolyte solution which, besides the metal electrolyte, comprises a reducing agent and optionally a halogenated polymer to be deposited in dispersed form.
摘要:
Oxidized waxes are obtainable by oxidation of polyolefins obtainable by means of metallocene catalysis and having a molecular weight Mw in the range from 1000 to 40,000 g/mol.
摘要:
A process for compressing ethylenically unsaturated monomers at a pressure of 200-5000 bar in the absence of a polymerization initiator comprises carrying out compression in the presence of a sterically hindered amine derivative.
摘要:
In a process for the polymerization of ethylene and optionally further monomers in a high-pressure reactor at from 120 to 350° C. and pressures of from 1000 to 4000 bar, hydrogen is intermittently introduced into the reactor.
摘要:
A catalyst composition suitable for the (co)polymerization of alk-1-enes is obtainable by mixing a metallocene complex with a C3-C20-alk-1-ene in an inert solvent, reacting the resulting mixture in a controlled manner with a compound capable of forming metallocenium ions and diluting the resulting mixture with an inert nonpolar, essentially aliphatic solvent, and also, if desired, applying the catalyst composition to a particulate support material.
摘要:
A catalyst solution for polymerizing &agr;-olefins is obtainable by reacting a metallocene compound with an activator compound which can react with the metallocene compound so as to displace a ligand from the central atom and stabilize the resulting cationic complex by a non-coordinating anion as an ion pair, adding one or more &agr;-olefins in a molar ratio of metallocene compound: &agr;-olefins of from 1:1 und 1:100 and mixing with at least 10 parts by volume of an aliphatic hydrocarbon.
摘要:
A process for preparing oxidized polyolefin waxes by reacting polyolefin waxes with oxygen or oxygen-containing gases at from 140 to 200° C. and at pressures of from 5 to 200 bar involves conducting the oxidation reaction continuously in a tube reactor but excludes the reaction of polyolefins prepared by metallocene catalysis.
摘要:
Copolymers of ethylene with .alpha.,.beta.-unsaturated carboxylic acids are prepared at from 50.degree. to 250.degree. C. and from 500 to 5000 bar in a stirred autoclave having a length/diameter ratio greater than 5:1 by a process in which the monomer mixtures are fed into the autoclave in at least two part-streams, the first part-stream being passed into the autoclave at the beginning of the autoclave pipe and the second part-stream being introduced at a position which is a distance away from the beginning which corresponds to 25-50% of the total length and the amount of the .alpha.,.beta.-unsaturated carboxylic acids in the first part-stream is from 20 to 90% less than the average amount in the further part-streams and a peroxide polymerization initiator having a lower decomposition temperature, or a mixture of peroxide polymerization initiators having a lower average decomposition temperature, than that of the initiators in the further part-streams is passed in with the first part-stream.