摘要:
A wholly aromatic polyester carbonate having a good color and excellent heat resistant stability. This polymer had an extremely low alkali metal content of 10 ppm or less. This polymer is advantageously produced by reacting an aromatic dicarboxylic acid, aromatic diol and diaryl carbonate in a specific molar ratio in the presence of a pyridine-based compound as a catalyst.
摘要:
A method for crystallizing a low molecular weight aromatic polycarbonate effectively and a method for preparing a polycarbonate resin having a desired intrinsic viscosity by using the polycarbonate crystallized with the above method of crystallization. A low molecular weight aromatic polycarbonate (preferably, the one produced by melt polycondensation) is crystallized by bringing it into contact with an aromatic monohydroxy compound or a mixture of said compound and water. Or, a low molecular weight aromatic polycarbonate is melt mixed with at least one or more kinds of compounds selected from the group consisting of aromatic monohydroxy compounds, carbonic acid diester compounds and aromatic dihydroxy compounds to crystallize the low molecular weight aromatic polycarbonate. The crystallized product is heated at a temperature lower than its melting point under reduced pressure or in an inert gas flow to convert it into a high polymerized state. Thus, a polycarbonate resin having a desired intrinsic viscosity is prepared.
摘要:
A process for producing a wholly aromatic polyester which is excellent in heat resistance, mechanical properties and yet color and has a high degree of polymerization by melt polymerizing a dicarboxylic acid and a diol directly on an industrial scale at a low cost in a short period of time without esterifying the dicarboxylic acid or diol in advance. To produce the wholly aromatic polyester by reacting and molding an aromatic dicarboxylic acid such as terephthalic acid, an aromatic diol such as 2,2-bis(4-hydroxyphenyl)propane and a diaryl carbonate by heating, a combination of a specific pyridine compound and an alkali metal (bi)carbonate, a combination of a specific pyridine compound and an organic tin compound or a specific titanium compound is existent as a catalyst. Thereby, the wholly aromatic polyester having the above properties is obtained.