摘要:
A gamma prime nickel-base superalloy and components formed therefrom that exhibit improved high-temperature dwell capabilities, including creep and hold time fatigue crack growth behavior. A particular example of a component is a powder metallurgy turbine disk of a gas turbine engine. The gamma-prime nickel-base superalloy contains, by weight, 18.0 to 30.0% cobalt, 11.4 to 16.0% chromium, up to 6.0% tantalum, 2.5 to 3.5% aluminum, 2.5 to 4.0% titanium, 5.5 to 7.5% molybdenum, up to 2.0% niobium, up to 2.0% hafnium, 0.04 to 0.20% carbon, 0.01 to 0.05% boron, 0.03 to 0.09% zirconium, the balance essentially nickel and impurities, wherein the titanium:aluminum weight ratio is 0.71 to 1.60.
摘要:
Components and methods of processing such components from precipitation-strengthened alloys so that the components exhibit desirable grain sizes following a supersolvus heat treatment. The method includes consolidating a powder of the alloy to form a billet having an average grain size. The billet is then forged at a temperature below the solvus temperature to form a forging having an average grain size of not coarser than the grain size of the billet. The billet is then forged at a total strain of at least 5%, after which at least a portion of the forging is heat treated at a temperature below the solvus temperature to pin grains within the portion. The entire forging can then be heat treated at a temperature above the solvus temperature of the alloy without coarsening the grains in the portion.
摘要:
Nickel based alloys are provided comprising from about 7.0 weight percent (wt %) to about 12.0 wt % chromium, from about 0.1 wt % to about 5 wt % molybdenum, from about 0.2 wt % to about 4.5 wt % titanium, from about 4 wt % to about 6 wt % aluminum, from about 3 wt % to about 4.9 wt % cobalt, from about 6.0 wt % to about 9.0 wt % tungsten, from about 4.0 wt % to about 6.5 wt % tantalum, from about 0.05 wt % to about 0.6 wt % hafnium, up to about 1.0 wt % niobium, up to about 0.02 wt % boron, and up to about 0.1 wt % carbon, with the remainder being nickel and incidental impurities. The alloys may be cast, directionally solidified and heat treated to provide articles having a gamma prime fraction of greater than about 50%.
摘要:
Nb—Si based alloy articles comprising a Nb—Si based alloy upon which is disposed an environmentally-resistant coating are described. They include a coating comprising at least one phase selected from the group consisting of M(Al,Si)3, M5(Al,Si)3, and M3Si5Al2, wherein M is one or more of Nb, Ti, Hf, Cr. Such coating can improve the environmental (e.g., in oxidation-promoting environments) resistance of a Nb—Si based alloy and alloy articles. Methods for preparing these articles are described as well.
摘要:
Coatings suitable for use as protective oxide-forming coatings on Nb-based substrates exposed to high temperatures and oxidative environments. The coatings contain chromium and/or molybdenum, preferably contains silicon, and optionally contains niobium, titanium, hafnium, iron, rhenium, tantalum, and/or tungsten, which in combination form multiple intermetallic phases, which in combination form one or more intermetallic phases that promote the formation of a slow-growing oxide scale. Depending on the particular coating composition, the intermetallic phases may be: a silicon-modified Cr2Nb Laves phase and optionally a chromium solid solution phase, a CrNbSi intermetallic phase, and/or an M3Si intermetallic phase where M is niobium, titanium, and/or chromium; or M5Si3, MSi2 and/or M3Si2 where M is molybdenum, niobium, titanium, chromium, hafnium, iron, rhenium, tantalum, and/or tungsten.
摘要翻译:适用于暴露于高温和氧化环境的Nb基基底上的保护性氧化物形成涂层的涂料。 涂层含有铬和/或钼,优选含有硅,并且任选地包含铌,钛,铪,铁,铼,钽和/或钨,其组合形成多个金属间相,其组合形成一个或多个金属间相 促进形成缓慢生长的氧化皮。 根据特定的涂料组合物,金属间相可以是:硅改性的Cr 2 Nb Laves相和任选的铬固溶相,CrNbSi金属间相和/或M3Si金属间相,其中M是铌,钛和/或 铬; 或M5Si3,MSi2和/或M3Si2,其中M是钼,铌,钛,铬,铪,铁,铼,钽和/或钨。
摘要:
Nickel based alloys are provided comprising from about 7.0 weight percent (wt %) to about 12.0 wt % chromium, from about 0.1 wt % to about 5 wt % molybdenum, from about 0.2 wt % to about 4.5 wt % titanium, from about 4 wt % to about 6 wt % aluminum, from about 3 wt % to about 4.9 wt % cobalt, from about 6.0 wt % to about 9.0 wt % tungsten, from about 4.0 wt % to about 6.5 wt % tantalum, from about 0.05 wt % to about 0.6 wt % hafnium, up to about 1.0 wt % niobium, up to about 0.02 wt % boron, and up to about 0.1 wt % carbon, with the remainder being nickel and incidental impurities. The alloys may be cast, directionally solidified and heat treated to provide articles having a gamma prime fraction of greater than about 50%.
摘要:
An article made of an alloy, and a method for making the article, are presented. The alloy is substantially free of martensite, and comprises the following composition: at least about 75 weight percent titanium; up to about 10 weight percent of a beta stabilizing component; from about 3 weight percent to about 15 weight percent of an alpha stabilizing component; and from about 0.05 weight percent to about 5 weight percent germanium. Another embodiment is a method for fabricating an article. The method comprises providing a billet made of an alloy as described above, and stabilizing the billet microstructure to form a stabilized billet; the method may further comprise superplastically processing the stabilized billet to form a processed item.
摘要:
A gamma prime nickel-base superalloy and components formed therefrom that exhibit improved high-temperature dwell capabilities, including creep and hold time fatigue crack growth behavior. A particular example of a component is a powder metallurgy turbine disk of a gas turbine engine. The gamma-prime nickel-base superalloy contains, by weight, 16.0 to 30.0% cobalt, 11.5 to 15.0% chromium, 4.0 to 6.0% tantalum, 2.0 to 4.0% aluminum, 1.5 to 6.0% titanium, up to 5.0% tungsten, 1.0 to 7.0% molybdenum, up to 3.5% niobium, up to 1.0% hafnium, 0.02 to 0.20% carbon, 0.01 to 0.05% boron, 0.02 to 0.10% zirconium, the balance essentially nickel and impurities, wherein the titanium:aluminum weight ratio is 0.5 to 2.0.
摘要:
A coating suitable for use as protective oxide-forming coatings on Nb-based substrates, and particularly monolithic niobium-based alloys, exposed to high temperatures and oxidative environments. The coating contains aluminum, may further contain silicon, and optionally contains niobium, titanium, hafnium, and/or chromium, which in combination form one or more intermetallic phases that promote the formation of a slow-growing oxide scale. The intermetallic phases may be M(Al,Si)3, M5(Al,Si)3, and/or M3Si5Al2 where M is niobium, titanium, hafnium, and/or chromium.
摘要:
Nb—Si based alloy articles comprising a Nb—Si based alloy upon which is disposed an environmentally-resistant coating are described. They include a coating comprising at least one phase selected from the group consisting of M(Al,Si)3, M5(Al,Si)3, and M3Si5Al2, wherein M is one or more of Nb, Ti, Hf, Cr. Such coating can improve the environmental (e.g., in oxidation-promoting environments) resistance of a Nb—Si based alloy and alloy articles. Methods for preparing these articles are described as well.