摘要:
The invention is directed to novel poly(ethcr-ester) polyols, processes for their production from monocarboxylic or polycarboxylic acid esters with one or more bound polyether chain(s). This invention also relates to the production of polyurethane materials in which the isocyanate-reactive component comprises these poly(ether-ester)polyols.
摘要:
Polyurea systems comprising: (a) an amino-functional aspartic ester of the general formula (I) wherein X represents an n-valent organic radical derived from a corresponding n-functional primary amine X(NH2)n, R1 and R2 each independently represent an organic radical having no Zerevitinov active hydrogens and n represents an integer of at least 2; and (b) an isocyanate functional prepolymer having a residual monomer content of less than 1% by weight, the prepolymer prepared by reacting: (b1) an aliphatic isocyante; and (b2) a polyol component having a number average molecular weight of ≧400 g/mol and an average OH functionality of 2 to 6, wherein the polyol component comprises one or more constituents selected from the group consisting of polyester polyols, polyester-polyether polyols and mixtures thereof; processes for making the same; postoperative adhesions barriers prepared therewith and dispensing systems for such polyurea systems.
摘要:
Light-stable, sinterable, thermoplastic polyurethanes with improved blooming behavior and good thermal stability as well as good technical processability are produced from an aliphatic diisocyanate using one or more chain extenders corresponding to a specified formula. These polyurethanes are particularly useful in the production of molded articles, particularly molded articles for automotive interiors.
摘要:
The present invention relates to a process for cleaning multi-product production plants for polyester polyols with a cleaning polyol. The cleaning polyol can be used as a raw material in the production of further polyols.
摘要:
Polyurethane elastomers having a defined node density are produced from specific polyetherester polyols. These elastomers are particularly useful for the production of microcellular and solid polyurethane elastomer components.
摘要:
The present invention relates to a novel process for the production of delayed action tin catalysts. This process comprises reacting a dialkyltin dihalide with an alkali metal sulfide, to yield the corresponding 2,2,4,4-tetrakis(alkyl)-1,3,2,4-dithia-stannetane catalyst.
摘要:
Polyols are conditioned and stabilized by mixing them at 0 to 150.degree. C. with from about 0.0001 to about 1% by weight, based on the quantity of polyol, of a silylated acid corresponding to the formula:X--[Si(CH.sub.3).sub.3 ].sub.nin whichX represents a neutral acid residue obtained by removal of the acidic hydrogen atoms from an n-basic acid having a maximum pKa value of 3, provided that the n-basic acid is not a hydrohalic acid andn represents an integer of from 1 to 3.The resultant polyol is characterized by good color and activity properties. The stabilized polyols are particularly useful in the production of polyurethanes, particularly polyurethane foams.
摘要:
The present invention relates to a method for producing a polyester polyol having a concentration of ether groups in the range from 9.0 mol/kg of polyester polyol to 22 mol/kg polyester polyol, characterized in that (i) in a first step (A) isophthalic acid, optionally in the form of a C1-C4 alkyl ester, and/or terephthalic acid, optionally in the form of a C1-C4 alkyl ester, is reacted with (B) oligoethylene glycol of the formula H—(OCH2CH2)n—OH having a numerical average number of oxyethylene groups n in the range from 3.0 to 9.0, in the presence of at least one catalyst selected from the group made up of tin(II) salts, bismuth(II) salts, and titanium tetraalkoxylates, at a temperature in the range from 160° C. to 240° C., and at a pressure in the range from 1 to 1013 mbar, for a duration in the range from 7 to 100 hours, and (ii) in a second step the reaction mixture resulting from step (i) is reacted with (C) phthalic acid and/or phthalic acid hydride, the polyester polyols obtained according to said method, and to the use thereof for producing PUR/PIR hard foam materials.
摘要:
The invention relates to stable emulsions for the production of foams based on isocyanate, at least comprising three polyols A1a, A1b and A1c as well as at least one physical blowing agent T, wherein A1a is a polyether polyol obtained by addition of epoxides to starter compounds selected from carbohydrates and di- or higher-functional alcohols, A1b is a polyether polyol started on an aromatic amine, and A1c is a polyester polyol obtained by esterification of a polycarboxylic acid component and a polyalcohol component, wherein the total amount of aromatic dicarboxylic acid derivatives used in the esterification, calculated on the basis of the free aromatic dicarboxylic acids and based on the total mass of polyalcohol component and polycarboxylic acid component, is less than or equal to 48.5% by mass.