摘要:
An off-axis cut of a nonpolar III-nitride wafer towards a polar (−c) orientation results in higher polarization ratios for light emission than wafers without such off-axis cuts. A 5° angle for an off-axis cut has been confirmed to provide the highest polarization ratio (0.9) than any other examined angles for off-axis cuts between 0 and 27°.
摘要:
A method of obtaining a hexagonal würtzite type epitaxial layer with a low impurity concentration of alkali-metal by using a hexagonal würtzite substrate possessing a higher impurity concentration of alkali-metal, wherein a surface of the substrate upon which the epitaxial layer is grown has a crystal plane which is different from the c-plane.
摘要:
An increase in the Indium (In) content in light-emitting layers of light-emitting diode (LED) structures prepared on nonpolar III-nitride substrates result in higher polarization ratios for light emission than LED structures containing lesser In content. Polarization ratios should be higher than 0.7 at wavelengths longer than 470 nm.
摘要:
A method for the fabrication of nonpolar indium gallium nitride (InGaN) films as well as nonpolar InGaN-containing device structures using metalorganic chemical vapor deposition (MOVCD). The method is used to fabricate nonpolar InGaN/GaN violet and near-ultraviolet light emitting diodes and laser diodes.
摘要:
Optical gain of a nonpolar or semipolar Group-III nitride diode laser is controlled by orienting an axis of light propagation in relation to an optical polarization direction or crystallographic orientation of the diode laser. The axis of light propagation is substantially perpendicular to the mirror facets of the diode laser, and the optical polarization direction is determined by the crystallographic orientation of the diode laser. To maximize optical gain, the axis of light propagation is oriented substantially perpendicular to the optical polarization direction or crystallographic orientation.
摘要:
A method for fabricating AlxGa1-xN-cladding-free nonpolar III-nitride based laser diodes or light emitting diodes. Due to the absence of polarization fields in the nonpolar crystal planes, these nonpolar devices have thick quantum wells that function as an optical waveguide to effectively confine the optical mode to the active region and eliminate the need for Al-containing waveguide cladding layers.
摘要翻译:一种用于制造Al x Ga 1-x N不包覆非极性III族氮化物基激光二极管或发光二极管的方法。 由于在非极性晶面中没有极化场,这些非极性器件具有用作光波导的厚量子阱,以有效地将光学模式限制在有源区,并且不需要含Al波导覆层。
摘要:
A high power blue-violet Ill-nitride semi-polar laser diode (LD) with an output power in excess of 1 W, a slope efficiency of more than 1 W/A, and an external quantum efficiency (EQE) in excess of 25% and more preferably, in excess of 35%. These operating characteristics make these laser diodes suitable for use in solid state lighting systems.
摘要翻译:输出功率超过1 W,斜率效率大于1 W / A,外部量子效率(EQE)超过25的高功率蓝紫色III族氮化物半极性激光二极管(LD) %,更优选超过35%。 这些工作特性使这些激光二极管适用于固态照明系统。
摘要:
A method for the fabrication of nonpolar indium gallium nitride (InGaN) films as well as nonpolar InGaN-containing device structures using metalorganic chemical vapor deposition (MOVCD). The method is used to fabricate nonpolar InGaN/GaN violet and near-ultraviolet light emitting diodes and laser diodes.
摘要:
A yellow Light Emitting Diode (LED) with a peak emission wavelength in the range 560-580 nm is disclosed. The LED is grown on one or more III-nitride-based semipolar planes and an active layer of the LED is composed of indium (In) containing single or multi-quantum well structures. The LED quantum wells have a thickness in the range 2-7 nm. A multi-color LED or white LED comprised of at least one semipolar yellow LED is also disclosed.