摘要:
The present invention provides a fiber having a nano-order fiber diameter, which is produced by without a process of dehydration and cyclization by a heat treatment after fiber spinning and has excellent heat resistance and mechanical strength, and a non-woven fabric composed of the fiber, and discloses the polyamide-imide fiber and the non-woven fabric having an average fiber diameter of from 0.001 μm to 1 μm and also discloses the process for producing threrof. The present invention also provides a separator for an electronic component which has a high conductivity and a small separator thickness and is improved in safety during reflow soldering or short-circuiting, and discloses the separator composed of a non-woven fabric obtained by an electro-spinning method.
摘要:
The present invention provides a fiber having a nano-order fiber diameter, which is produced by without a process of dehydration and cyclization by a heat treatment after fiber spinning and has excellent heat resistance and mechanical strength, and a non-woven fabric composed of the fiber, and discloses the polyamide-imide fiber and the non-woven fabric having an average fiber diameter of from 0.001 μm to 1 μm and also discloses the process for producing threrof. The present invention also provides a separator for an electronic component which has a high conductivity and a small separator thickness and is improved in safety during reflow soldering or short-circuiting, and discloses the separator composed of a non-woven fabric obtained by an electro-spinning method.
摘要:
The easy-to-tear stretched aliphatic polyester film of the present invention is characterized in that the edge tear strength in the longitudinal direction and the transverse direction is not more than 22 N. The easy-to-tear stretched aliphatic polyester film of the present invention is produced by a method of irradiation of actinic rays on an aliphatic polyester film or a method of film-forming a film obtained by laminating aliphatic polyesters having different melting points in three layers of A/B/A under particular film-forming conditions.
摘要翻译:本发明的容易撕裂的拉伸脂肪族聚酯膜的特征在于,纵向和横向的边缘撕裂强度不大于22N。本发明的容易撕裂的拉伸脂肪族聚酯膜 本发明通过在脂肪族聚酯膜上照射光化学射线的方法或通过在特定的成膜条件下层压三层A / B / A的不同熔点的脂肪族聚酯而成膜的方法来制造。
摘要:
The present invention is a heat-resistant film comprising at least any one of a polybenzazole, aramid and polyamideimide produced by introducing a thin film made by a roll, slit or press from a polymer solution sandwiched between at least two supports into a coagulating bath and peeling the supports off in the coagulating bath to effect the coagulation, and a composite ion-exchange membrane having a surface layer consisting of an ion-exchange resin excluding a porous film on the both side of a composite layer formed by impregnating said film with the ion-exchange resin. A heat-resistant film having a combination of excellent heat resistance, mechanical strength, smoothness and interlaminar peeling resistance, especially a microporous heat-resistant film, and a composite ion-exchange membrane employing the same which has an excellent ion conductivity are provided.
摘要:
A detector (29) detects that a refrigerant gas has leaked from a refrigeration cycle, or detects in advance that a refrigerant is to leak. The alarming device (27) gives users an alarming signal warning against the refrigerant leak. The alarming device (27) is caused to stop giving an alarming signal after users open doors of storage compartments including a refrigerator compartment (4), a vegetable storage compartment (5) and a freezer compartment (6). For example, after all the doors of the storage compartments are opened, giving the alarming signal is stopped. Otherwise, giving the alarming signal is stopped after the door of a storage compartment into which cold air flows by causing a damper (12) to open is opened.
摘要:
The present invention provides a process for producing a precursor fiber which can provide a carbon fiber having high strength and high elastic modulus. The process of the present invention comprises a step where an aqueous solution of amphoteric molecule is prepared; a step where carbon nanotube is added to the aqueous solution of the amphoteric molecule so that the carbon nanotube is dispersed therein to prepare a dispersion of carbon nanotube; a step where the carbon nanotube dispersion is mixed with a polyacrylonitrile polymer and rhodanate or zinc chloride to prepare a spinning dope; a step where a coagulated yarn is prepared from the spinning dope by a wet or dry-wet spinning method; and a step where the coagulated yarn is drawn to give a precursor fiber for carbon fiber.
摘要:
The easy-to-tear stretched aliphatic polyester film of the present invention is characterized in that the edge tear strength in the longitudinal direction and the transverse direction is not more than 22 N. The easy-to-tear stretched aliphatic polyester film of the present invention is produced by a method of irradiation of actinic rays on an aliphatic polyester film or a method of film-forming a film obtained by laminating aliphatic polyesters having different melting points in three layers of A/B/A under particular film-forming conditions.
摘要翻译:本发明的容易撕裂的拉伸脂肪族聚酯膜的特征在于,纵向和横向的边缘撕裂强度不大于22N。本发明的容易撕裂的拉伸脂肪族聚酯膜 本发明通过在脂肪族聚酯膜上照射光化学射线的方法或通过在特定的成膜条件下层压三层A / B / A的不同熔点的脂肪族聚酯而成膜的方法来制造。