摘要:
A magnetic paint is prepared by a method comprising a surface-treating step for magnetic powder, to obtain a first composition by mixing and stirring a composition which comprises a magnetic powder, a dispersant and/or a binder resin, and an organic solvent, and which contains 40% by weight or less of a non-solvent component, while applying a shear force to the composition; and a concentrating step to obtain a second composition by concentrating the first composition until the content of the non-solvent components of the first composition reaches 80% by weight or more.
摘要:
A magnetic recording medium with excellent high density recording performances and good durability comprising a non-magnetic substrate, a non-magnetic layer containing a non-magnetic powder and a binder formed on the non-magnetic substrate, and a magnetic layer having a thickness of less than 100 nm and containing a substantially particulate non-magnetic powder, a substantially particulate magnetic powder having an average particle size of less than 25 nm, and a binder, wherein an average particle size R of the non-magnetic powder contained in the magnetic layer and a thickness D of the magnetic powder satisfy the following relationship: 0.88≦R/D≦2.5.
摘要翻译:一种具有优异的高密度记录性能和良好耐久性的磁记录介质,包括非磁性基板,含有非磁性粉末的非磁性层和形成在非磁性基板上的粘合剂,以及具有厚度为 小于100nm,并且含有基本上颗粒的非磁性粉末,平均粒度小于25nm的基本上颗粒的磁性粉末和粘合剂,其中包含在磁性材料中的非磁性粉末的平均粒径R 层和磁粉的厚度D满足以下关系:0.88≦̸ R / D≦̸ 2.5。
摘要:
A magnetic tape comprising a non-magnetic support, a primer layer formed on one surface of the support, a magnetic layer formed on the primer layer, and a back layer formed on the other surface of the support, in which the tape has a total thickness of 4.0 to 5.4 μm, at least one of the primer layer and the magnetic layer contains a fatty acid amide, and an amount of the fatty acid amide extracted from the side of the magnetic layer with n-hexane is from 0.5 to 1.5 mg/cm3.
摘要:
A magnetic paint is prepared by a method comprising a surface-treating step for magnetic powder, to obtain a first composition by mixing and stirring a composition which comprises a magnetic powder, a dispersant and/or a binder resin, and an organic solvent, and which contains 40% by weight or less of a non-solvent component, while applying a shear force to the composition; and a concentrating step to obtain a second composition by concentrating the first composition until the content of the non-solvent components of the first composition reaches 80% by weight or more.
摘要:
A magnetic recording medium with excellent high density recording performances and good durability comprising a non-magnetic substrate, a non-magnetic layer containing a non-magnetic powder and a binder formed on the non-magnetic substrate, and a magnetic layer having a thickness of less than 100 nm and containing a substantially particulate non-magnetic powder, a substantially particulate magnetic powder having an average particle size of less than 25 nm, and a binder, wherein an average particle size R of the non-magnetic powder contained in the magnetic layer and a thickness D of the magnetic powder satisfy the following relationship: 0.88≦R/D≦2.5.
摘要翻译:一种具有优异的高密度记录性能和良好耐久性的磁记录介质,包括非磁性基板,含有非磁性粉末的非磁性层和形成在非磁性基板上的粘合剂,以及具有厚度为 小于100nm,并且含有基本上颗粒的非磁性粉末,平均粒度小于25nm的基本上颗粒的磁性粉末和粘合剂,其中包含在磁性材料中的非磁性粉末的平均粒径R 层和磁粉的厚度D满足以下关系:0.88 <= R / D <= 2.5。
摘要:
A magnetic tape comprising a non-magnetic support, a primer layer formed on one surface of the support, a magnetic layer formed on the primer layer, and a back layer formed on the other surface of the support, in which the tape has a total thickness of 4.0 to 5.4 μm, at least one of the primer layer and the magnetic layer contains a fatty acid amide, and an amount of the fatty acid amide extracted from the side of the magnetic layer with n-hexane is from 0.5 to 1.5 mg/cm3.
摘要翻译:一种磁带,包括非磁性载体,形成在载体的一个表面上的底漆层,形成在底漆层上的磁性层,以及形成在载体的另一个表面上的背层,其中胶带具有总共 厚度为4.0〜5.4μm,底层和磁性层中的至少一层含有脂肪酸酰胺,使用正己烷从磁性层一侧提取的脂肪酸酰胺的量为0.5〜1.5mg / cm 3。