摘要:
Interpolymers of aromatic polyesters and cross-linked (or partially cross-linked) rubbers and a process for their production in which a mixture of a cross-linked rubber in latex form containing reactive groups and an aqueous solution of an alkali metal or alkaline earth metal diphenolate is reacted with a solution of a dicarboxylic acid halide and/or a carbonyl halide in a water-immiscible solvent so that an aromatic polyester forms at the water/organic solvent phase boundary, which polyester goes over into the organic phase and the rubber at the same time also goes into the organic phase. The interpolymer of rubber and organic polyester thus formed is suitable for the production of moulded articles of all kinds by the methods of thermoplastic shaping such as extrusion and injection moulding.
摘要:
Thermoplastic polydiorganosiloxane/polycarbonate block copolymers based on dihydroxydiphenylcycloalkanes corresponding to the following general formula (I): ##STR1## wherein R.sup.1 and R.sup.2 independently represent hydrogen, halogen, preferably chlorine or bromine, C.sub.1 -C.sub.8 alkyl, C.sub.5 or C.sub.6 cycloalkyl, C.sub.5 -C.sub.10 aryl or C.sub.7 -C.sub.12 aralkyl, preferably phenyl-C.sub.1 -C.sub.4 -alkyl, in particular benzyl: m represents an integer of from 4 to 7, preferably 4 or 5;R.sup.3 and R.sup.4 may be chosen individually for each X and independently represent hydrogen or C.sub.1 -C.sub.12 alkyl; andX represents carbon; with the proviso that R.sup.3 and R.sup.4 both represent alkyl on at least one atom X,having an average molecular weight M.sub.w (weight average) of 10 000 to 300 000, a content of aromatic polycarbonate of 21 to 99.5% by weight and a content of polyorganosiloxane of 79 to 0.5% by weight.
摘要:
The new bisesters of unsaturated carboxylic acids corresponding to the following formula ##STR1## may be used in curable polyester resin mixtures which may in turn be used for the production of moldings. The curable mixtures obtainable from the new bisesters of unsaturated carboxylic acids show a higher glass transition temperature than normal polyester resins and, despite a higher crosslink density, show broader-mesh crosslinking.
摘要:
This invention relates to thermoplastic molding compositions having improved impact strength at low temperatures comprising polyamides and grafted, at least partially crosslinked diene rubbers and/or acrylate rubbers having a bimodal rubber particle size distribution.
摘要:
A process for the production of cross-linked graft copolymers by the radically initiated precipitation copolymerization of an ethylene/vinyl ester copolymer as graft base and a mixture to be grafted of one or more aromatic monovinyl compounds, acrylonitrile and/or methacrylonitrile, a cross-linking agent containing two or more carbon-carbon double bonds, and, optionally, another monoolefinically unsatured copolymerizable monomer wherein the ungrafted base is precipitated by the addition of a precipitating agent simultaneously with the precipitating cross-linked graft copolymer.
摘要:
The use of a liquid polymethyl phenyl siloxane or a liquid polydimethyl siloxane, in combination with calcium stearate, pentaerythritol tetrastearate, bis-stearylamide of ethylene diamine or mixtures thereof for improving the physical properties of ABS-polymers.
摘要:
The invention relates to the use of mixtures consisting of 5 to 95% by weight of an aromatic polycarbonate of which the linear chains contain from 0.1 mol-% to 50 mol-% bifunctional structural units corresponding to formula (1) ##STR1## and 95 to 5% by weight of a thermoplastic styrene polymer and, optionally, standard additives as substrates for optical storage media.
摘要:
Molding compositions comprising a "terminally unsaturated"polyurethane, a copolymerizable vinyl or vinylidene compound and a rubbery-elastic polymer having a glass transition temperature of between -90.degree. and +10.degree. C. can be used for the preparation of molded articles having a considerably increased impact strength and a good heat distortion temperature, strength and rigidity.