摘要:
A method for forming a quaternary alloy film of Co—W—P—Au for use as a diffusion barrier layer on a copper interconnect in a semiconductor structure and devices formed incorporating such film are disclosed. In the method, a substrate that has copper conductive regions on top is first pre-treated by two separate pre-treatment steps. In the first step, the substrate is immersed in a H2SO4 rinsing solution and next in a solution containing palladium ions for a length of time sufficient for the ions to deposit on the surface of the copper conductive regions. The substrate is then immersed in a solution that contains at least 15 gr/l sodium citrate or EDTA for removing excess palladium ions from the surface of the copper conductive regions. After the pre-treated substrate is rinsed in a first rinsing step by distilled water, the substrate is electroless plated a Co—W—P film on the surfaces of the copper conductive regions in a first plating solution that contains cobalt ions, tungstate ions, citrate ions and a reducing agent. After the substrate coated with the Co—W—P film is rinsed in a second rinsing step by distilled water, the substrate is immersed in a second electroless plating solution for depositing a Au layer on top of the Co—W—P film. The present invention novel quaternary alloy film can be used as an effective diffusion barrier layer between a copper interconnect and silicon substrate or SiO2 dielectric layers.
摘要:
A method for forming a quaternary alloy film of Co—W—P—Au for use as a diffusion barrier layer on a copper interconnect in a semiconductor structure and devices formed incorporating such film are disclosed. In the method, a substrate that has copper conductive regions on top is first pre-treated by two separate pre-treatment steps. In the first step, the substrate is immersed in a H2SO4 rinsing solution and next in a solution containing palladium ions for a length of time sufficient for the ions to deposit on the surface of the copper conductive regions. The substrate is then immersed in a solution that contains at least 15 gr/l sodium citrate or EDTA for removing excess palladium ions from the surface of the copper conductive regions. After the pre-treated substrate is rinsed in a first rinsing step by distilled water, the substrate is electroless plated a Co—W—P film on the surfaces of the copper conductive regions in a first plating solution that contains cobalt ions, tungstate ions, citrate ions and a reducing agent. After the substrate coated with the Co—W—P film is rinsed in a second rinsing step by distilled water, the substrate is immersed in a second electroless plating solution for depositing a Au layer on top of the Co—W—P film. The present invention novel quaternary alloy film can be used as an effective diffusion barrier layer between a copper interconnect and silicon substrate or SiO2 dielectric layers.
摘要:
The idea of the invention is to coat the free surface of patterned Cu conducting lines in on-chip interconnections (BEOL) wiring by a 1-20 nm thick metal layer prior to deposition of the interlevel dielectric. This coating is sufficiently thin so as to obviate the need for additional planarization by polishing, while providing protection against oxidation and surface, or interface, diffusion of Cu which has been identified by the inventors as the leading contributor to metal line failure by electromigration and thermal stress voiding. Also, the metal layer increases the adhesion strength between the Cu and dielectric so as to further increase lifetime and facilitate process yield. The free surface is a direct result of the CMP (chemical mechanical polishing) in a damascene process or in a dry etching process by which Cu wiring is patterned. It is proposed that the metal capping layer be deposited by a selective process onto the Cu to minimize further processing. We have used electroless metal coatings, such as CoWP, CoSnP and Pd, to illustrate significant reliability benefits, although chemical vapor deposition (CVD) of metals or metal forming compounds can be employed.
摘要:
The idea of the invention is to coat the free surface of patterned Cu conducting lines in on-chip interconnections (BEOL) wiring by a 1-20 nm thick metal layer prior to deposition of the interlevel dielectric. This coating is sufficiently thin so as to obviate the need for additional planarization by polishing, while providing protection against oxidation and surface, or interface, diffusion of Cu which has been identified by the inventors as the leading contributor to metal line failure by electromigration and thermal stress voiding. Also, the metal layer increases the adhesion strength between the Cu and dielectric so as to further increase lifetime and facilitate process yield. The free surface is a direct result of the CMP (chemical mechanical polishing) in a damascene process or in a dry etching process by which Cu wiring is patterned. It is proposed that the metal capping layer be deposited by a selective process onto the Cu to minimize further processing. We have used electroless metal coatings, such as CoWP, CoSnP and Pd, to illustrate significant reliability benefits, although chemical vapor deposition (CVD) of metals or metal forming compounds can be employed.