摘要:
A process for producing a grain-oriented electrical steel sheet having improved magnetic and surface film properties, comprising: using an electrical silicon steel slab containins S in an extremely small amount of 0.012 wt % or less and Mn in a limited range of 0.08 to 0.45 wt %; heating the slab to a relatively low temperature of not higher than 1200.degree. C.; hot-rolling the slab to form a hot-rolled strip; cold-rolling the strip to a thickness of a final product sheet; decarburization-annealing the cold-rolled strip; nitriding the strip while it is travelling; applying an annealing separator to the strip; and final texture-annealing the strip by heating the strip to a first temperature of from 800.degree. to 850.degree. C. in an atmosphere of (N.sub.2 +Ar).gtoreq.30 vol % with 25 vol % or more N.sub.2 and the remainder H.sub.2 and subsequently heating from the first temperature to above 1200.degree. C. in a conventional atmosphere.
摘要:
Grain oriented silicon steel sheet on which is formed an insulating coating having a thickness that is not less than 2.5 .mu.m that imparts tension to the steel sheet which does not have an inorganic mineral layer formed during a final annealing step (glass film) and a method of forming on grain oriented silicon steel sheet an insulating coating that is not less than 2.5 .mu.m thick and which imparts tension to the steel sheet which does not have the inorganic mineral layer (glass film) that forms during finish annealing, and a method of forming a tensioning insulating coating on grain oriented silicon steel sheet which has been finish annealed and does not have an inorganic mineral surface layer (glass film), after first forming a layer of SiO.sub.2 not less than 0.001 .mu.m thick on the oriented silicon steel sheet.
摘要:
The present invention provides a grain-oriented electrical steel sheet product having a superior corrosion resistance, annealing resistance, film tension, and the like in insulating treatment based on a phosphate not containing chromium and a treatment agent for the same, so provides grain-oriented electrical steel sheet having an insulating film not containing chromium characterized by the insulating film containing a phosphate and one or more compounds selected from inorganic compounds of Fe, Ni, Co, Cu, Sr, and Mo in an amount, as metal elements, of 0.06 to 2.10 moles per mole of phosphate, and an insulating film agent of the same.
摘要:
The present invention provides a grain-oriented electrical steel sheet product having a superior corrosion resistance, annealing resistance, film tension, and the like in insulating treatment based on a phosphate not containing chromium and a treatment agent for the same, so provides grain-oriented electrical steel sheet having an insulating film not containing chromium characterized by the insulating film containing a phosphate and one or more compounds selected from inorganic compounds of Fe, Ni, Co, Cu, Sr, and Mo in an amount, as metal elements, of 0.06 to 2.10 moles per mole of phosphate, and an insulating film agent of the same.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
A process for producing a grain-oriented steel sheet having superior magnetic and surface film characteristics, which comprises the steps of: heating to a temperature of 1200.degree. C. or lower an electrical steel slab comprising 0.025 to 0.075 wt % C, 2.5 to 4.5 wt % Si, 0.012 wt % or less S, 0.010 to 0.060 wt % acid-soluble Al, 0.010 wt % or less N, 0.080 to 0.045 wt % Mn, and the balance consisting of Fe and unavoidable impurities; hot-rolling the heated slab to form a hot-rolled steel sheet; cold-rolling the hot-rolled sheet to a final product sheet thickness by single cold rolling step or by two or more steps of cold rolling with an intermediate annealing therebetween; decarburization-annealing the cold-rolled sheet under a condition such that decarburization alone is effected until primary-recrystallized grains grow to an average grain size of at least 15 .mu.m, and thereafter, concurrently effecting a decarburization and nitriding; applying an annealing separator to the decarburization-annealed sheet; and final-annealing the annealing separator-applied sheet.
摘要:
A negative electrode active material for an electric device includes an alloy containing Si in a range of greater than or equal to 27% by mass and less than 100% by mass, Sn in a range of greater than 0% by mass and less than or equal to 73% by mass, V in a range of greater than 0% by mass and less than or equal to 73% by mass, and inevitable impurities as a residue. The negative electrode active material can be obtained with, for example, a multi DC magnetron sputtering apparatus by use of Si, Sn, and V as targets. An electric device using the negative electrode active material can achieve long cycle life and ensure a high capacity and cycle durability.
摘要:
Disclosed is a negative electrode active material for electrical devices, comprising an alloy having a composition represented by the formula: SixCyAlz. In the composition formula: SixCyAlz, x, y and z represent mass percent values and satisfy the following conditions: x+y+z=100; 36≦x
摘要翻译:公开了一种电气器件用负极活性物质,其包含具有由下式表示的组成的合金:SixCyAlz。 在组成式中:SixCyAlz,x,y和z表示质量百分数值,满足以下条件:x + y + z = 100; 36 @ x <100; 0