This invention relates to a single- or multilayer, oriented film formed from polyester and at least one inorganic black pigment. The inventive films include at least one layer which has, alongside polyester, an amount of from 0.5 to 75% by weight of particles incorporating iron oxide as black pigment.
摘要:
This invention relates to a single- or multilayer, oriented film formed from polyester and at least one inorganic black pigment. The inventive films include at least one layer which has, alongside polyester, an amount of from 0.5 to 75% by weight of particles incorporating iron oxide as black pigment.
摘要:
The invention relates to a hydrolysis-stable polyester film comprising a polyester, whose thickness is preferably in the range from 0.4 to 500 μm. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.
摘要:
The invention relates to a single- or multilayer, oriented film in which at least one layer is comprised of a thermoplastic polymer having a minimum amount of amide groups. The polymer is a polyester, a polyamide, or a mixture comprised of polyester and polyamide, or is a copolymer comprised of these two materials. The film also comprises a component a) which, when irradiated with electromagnetic or particulate radiation, forms metal nuclei onto which further metal can be accumulated in further steps of the process. The invention also relates to a process for the production of this film, and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, or film-based circuits of any type.
摘要:
The invention relates to a single- or multilayer, oriented film in which at least one layer is comprised of a thermoplastic polymer having a minimum amount of amide groups. The polymer is a polyester, a polyamide, or a mixture comprised of polyester and polyamide, or is a copolymer comprised of these two materials. The film also comprises a component a) which, when irradiated with electromagnetic or particulate radiation, forms metal nuclei onto which further metal can be accumulated in further steps of the process. The invention also relates to a process for the production of this film, and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, or film-based circuits of any type.
摘要:
The invention relates to a hydrolysis-stable polyester film comprising a polyester, whose thickness is preferably in the range from 0.4 to 500 μm. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.
摘要:
The invention relates to a single- or multilayer, oriented, film coated with an aminosilane compound and composed of polyester which comprises an additive which, on irradiation with electromagnetic radiation, forms metal nuclei on which further metal can be deposited in further steps of the process. The invention further relates to a process for producing this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits of any type.
摘要:
The invention relates to a single- or multilayer, oriented, film coated with an aminosilane compound and composed of polyester which comprises an additive which, on irradiation with electromagnetic radiation, forms metal nuclei on which further metal can be deposited in further steps of the process. The invention further relates to a process for producing this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits of any type.
摘要:
The invention relates to a hydrolysis-stable polyester whose thickness is preferably in the range from 0.4 to 500 μm. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.
摘要:
The invention relates to a hydrolysis-stable polyester whose thickness is preferably in the range from 0.4 to 500 μm. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.