摘要:
A white toner has a first temperature range not less than 25° C. in which 60° glossiness is 10 or less between a fixable minimum temperature and a fixable maximum temperature thereof. The white toner has a second temperature range not less than 25° C. in which 60° glossiness is from 30 to 60 therebetween.
摘要:
A toner, where a diffraction peak of the toner as measured by X-ray diffraction spectroscopy is present at least in a region where 2θ is from 20° through 25°, and a difference between Tg1 and Tg2 is 10° C. or less, where Tg1 is a glass transition temperature of the toner, as observed in a last heating step, when heating and cooling are performed on the toner by means of a differential scanning calorimeter (DSC) under the heating and cooling conditions 1 defined in the specification, and Tg2 is a glass transition temperature of the toner, as observed in a last heating step, when heating and cooling are performed on the toner by means of the differential scanning calorimeter (DSC) under the heating and cooling conditions 2 defined in the specification.
摘要:
A toner for electrophotography, the toner including an amorphous polyester resin, an addition polymerization-based resin, and wax that is ester wax or carnauba wax, wherein the toner satisfies relationships represented by Formula 1 and Formula 2 below, SPr>SPw>SPd (Formula 1) |SPr−SPw|>|SPw−SPd| (Formula 2) where SPr is a value of a solubility parameter of the amorphous polyester resin, SPw is a value of a solubility parameter of the wax, and SPd is a value of a solubility parameter of the addition polymerization-based resin.
摘要:
Provided is a toner including toner particles, each toner particle includes: a base particle including a binder resin; and external additive particles, wherein the external additive particles include particles each having an equivalent circle diameter of 10 nm or greater, a volume average particle diameter of the particles each having an equivalent circle diameter of 10 nm or greater is 80 nm or greater but 140 nm or less, and a ratio (circumscribed circle area/particle area) of a circumscribed circle area of the particle having an equivalent circle diameter of 10 nm or greater to a particle area of the particle having an equivalent circle diameter of 10 nm or greater is 1.60 or greater but 2.60 or less.
摘要:
A toner is provided. The toner comprises mother particles and an external additive covering the mother particles. The mother particles comprise a binder resin, and the external additive comprises inorganic particles. The inorganic particles comprise small-size inorganic particles having an equivalent circle diameter of from 30 to 70 nm and large-size inorganic particles having an equivalent circle diameter of from 150 to 200 nm and a circularity of 0.85 or more. The large-size inorganic particles are 20 to 70 in number per 100 μm2 image area of the toner observed with a field-emission scanning electron microscope.
摘要:
To provide an electrophotographic toner, which contains a crystalline resin, a non-crystalline resin, a colorant, and a releasing agent, wherein the toner has a storage elastic modulus of 5.0×104 Pa to 5.0×106 Pa at 80° C., and a storage elastic modulus of 2.0×102 Pa to 2.0×103 Pa at 140° C., and wherein the toner has a ratio (C)/((C)+(A)) of 0.10 or greater, where (C) is an integrated intensity of a diffraction spectrum derived from a crystalline structure, (A) is an integrated intensity of a diffraction spectrum derived from a non-crystalline structure, and the diffraction spectrum is a diffraction spectrum of the toner as measured by an X-ray diffraction spectrometer.
摘要:
To provide a toner, containing: a noncrystalline resin; and a crystalline resin, wherein the crystalline resin has a weight average molecular weight of 100,000 to 180,000, wherein a temperature range of the toner, within which a loss tangent (tan δ) as measured by a dynamic viscoelasticity measurement is 6 or greater, is 20° C. or greater, and wherein a fixed toner image has 60° glossiness of 30 to 50, where the fixed toner image is obtained by forming an unfixed toner image having a deposition amount of 0.4 mg/cm2 on a recording medium having 60° glossiness of 30 for a measurement, and fixing at temperature at which temperature of the toner image is a lowest temperature of the temperature range +10° C., at 0.15 MPa, for a nipping duration of 50 msec.
摘要翻译:提供一种调色剂,其含有:非结晶性树脂; 和结晶性树脂,其中所述结晶性树脂的重均分子量为100,000〜180,000,其中通过动态粘弹性测定测定的损耗角正切(tanδ)为6以上的调色剂的温度范围为 20℃或更高,并且其中固定的调色剂图像具有30至50的光泽度为30°,其中定影的调色剂图像通过在具有60nm的记录介质上形成具有0.4mg / cm 2的沉积量的未定影调色剂图像 °光泽度为30,并且在调色剂图像的温度为温度范围+ 10℃的最低温度的温度下,在0.15MPa下固定,夹持持续时间为50毫秒。
摘要:
A toner is provided. The toner includes a core particle, a second shell layer overlying the core particle, and a first shell layer overlying the second shell layer and constituting an outermost layer. The second shell layer includes a crystalline resin, and the first shell layer includes an amorphous resin.
摘要:
White toner contains a binder resin, a white pigment, and a releasing agent, wherein the white pigment is coated with the releasing agent and dispersed in the binder resin.
摘要:
A toner is provided. The toner comprises a binder resin, a release agent, and a function imparting agent comprising a fatty acid amide having a melting point of from 110 to 160 degrees C. When the toner is heated by a differential scanning calorimeter, the toner exhibits no endothermic peak within a temperature range of ±20 degrees C. of a temperature at a highest endothermic peak derived from the fatty acid amide.