摘要:
A polylactic acid-based resin composition comprising: 50-90 mass % of a polylactic acid-based resin (A); and 10-50 mass % of a polyolefin-based resin (B), heat quantity of crystallization of the polyolefin-based resin (B) being 40 J/g or less as measured by using differential scanning calorimeter as measured at a thermal process comprising the steps of: heating up to 200° C. at a heating rate of 10° C./min; keeping the temperature at 200° C. for 5 minutes; and cooling down to the room temperature at a cooling rate of 10° C./min. The invention also provides: The composition may be applied, for example, to produce a polylactic acid-based film, a molded product using the film, an elongated film, a heat-shrinkable label, and a container having the heat-shrinkable label.
摘要:
There is provided an encapsulant material for solar cells which facilitates production of a solar cell module and is excellent in flexibility, heat resistance, transparency, etc., and a solar cell module produced using the encapsulant material. The present invention relates to an encapsulant material for solar cells which includes a resin composition (C) containing an ethylene-α-olefin random copolymer (A) capable of satisfying the following condition (a) and an ethylene-α-olefin block copolymer (B) capable of satisfying the following condition (b): (a) a heat of crystal fusion is from 0 to 70 J/g as measured in differential scanning calorimetry at a heating rate of 10° C./min; and (b) a crystal fusion peak temperature is 100° C. or higher and a heat of crystal fusion is from 5 to 70 J/g as measured in differential scanning calorimetry at a heating rate of 10° C./min.
摘要:
A diaphragm for electro-acoustic transducers, especially a diaphragm for speakers, and a film for the diaphragm excellent in the formability and the durability in high-output operation are obtained. A diaphragm for electro-acoustic transducers formed of a film that contains a polybiphenyl ether sulfone resin (A) having a specific repetitive unit or contains it and a crystalline resin (B) such as polyaryl ketone resin; and a film for use for the diaphragm.
摘要:
A film of a resin composition comprising total 100 parts by weight of a crystalline polyarylketone resin (A) and a noncrystalline polyetherimide resin (B), and 5 to 50 parts by weight of a filler, said film satisfies the following relation Tc(A)
摘要:
There is provided a packaging film which has a good suitability for use in an automatic packaging machine, and is free from occurrence of sagging even when stored in a low-temperature condition for a long period of time as well as hardly suffers from occurrence of whitening when subjected to high stretch packaging. The stretch packaging film of the present invention comprises a laminated film having at least three layers comprising opposite surface layers each comprising an ethylene-based resin (A) as a main component and an intermediate layer comprising a propylene-based resin (C) and a propylene-based resin (B) which respectively satisfy specific conditions, at a specific compounding ratio, and having a heat of crystallization (ΔHc) of 10 to 60 J/g as measured at a temperature drop rate of 10° C./min using a differential scanning calorimeter (DSC) and a storage elastic modulus (E′) at 20° C. of 100 MPa to 1 GPa as measured with respect to the laminated film at an oscillation frequency of 10 Hz and a distortion of 0.1% by a dynamic viscoelasticity measuring method.
摘要:
Provided are a sheet for a solar cell of a monolayer construction or a multilayer construction based on a polyphenylene ether-based resin layer formed of a resin composition using a polyphenylene ether as a main component, which has excellent durability, excellent flame retardancy, excellent dimensional stability and high adhesiveness with a encapsulating resin layer or the like, and a solar cell module obtained by providing the sheet for a solar cell.
摘要:
A heat-shrinkable polyolefin series laminated film having excellent firmness (stiffness at ordinary temperature) of film, resistance to fingerprint bleaching, shrink finishability, transparency and regeneration additivity, with a small natural shrinkage and accurately separable by specific gravity, can be provided by, in a laminated film provided with a surface layer (I) and an intermediate layer (III), forming the surface layer (I) with a mixed resin of cyclic olefin series resin and a polyethylene series resin (A) with a Tm of 80° C. or higher but no greater than 125° C. as a main component, and, forming the intermediate layer (III) with a resin composition having as a main component a cyclic olefin series resin, preferably a mixed resin composition of a cyclic olefin series resin and a polyethylene series resin (C) with a Tm exceeding 125° C. but no greater than 140° C., as a main component.
摘要:
A heat-shrinkable polyolefin series laminated film having excellent firmness (stiffness at ordinary temperature) of film, resistance to fingerprint bleaching, shrink finishability, transparency and regeneration additivity, with a small natural shrinkage and accurately separable by specific gravity, can be provided by, in a laminated film provided with a surface layer (I) and an intermediate layer (III), forming the surface layer (I) with a mixed resin of cyclic olefin series resin and a polyethylene series resin (A) with a Tm of 80° C. or higher but no greater than 125° C. as a main component, and, forming the intermediate layer (III) with a resin composition having as a main component a cyclic olefin series resin, preferably a mixed resin composition of a cyclic olefin series resin and a polyethylene series resin (C) with a Tm exceeding 125° C. but no greater than 140° C., as a main component.
摘要:
A heat resistant film comprising total 100 parts by weight of a resin composition comprising at least (A-1) a polyetherimide resin having repeating units of the structural formula (1), (A-2) a polyetherimide resin having repeating units of the structural formula (2), and (B) a polyarylketone resin having a melting peak temperature of 260 degrees C. or higher, and 5 to 50 parts by weight of a filler, wherein a weight ratio of the resin components, [(A-1)+(A-2)]/(B)], ranges from 70/30 to 30/70 and a weight ratio, (A-1)/(A-2), ranges from
摘要:
Provided are a solar cell encapsulant material which facilitates production of solar cell modules, which does not require a crosslinking step and which is excellent in heat resistance and others, and a solar cell module produced by the use of the encapsulant material. The solar cell encapsulant material comprises a resin composition (C) that contains an olefin-based polymer (A) satisfying the following requirement (a) and an olefin-based polymer (B) satisfying the following requirement (b). (a) The crystal melting peak temperature of the polymer, as measured at a heating rate of 10° C./min in differential scanning calorimetry, is lower than 100° C. (b) The extrapolated onset temperature of melting of the polymer, as measured at a heating rate of 10° C./min in differential scanning calorimetry, is 100° C. or higher.