A toner including toner particles including a binder resin; a colorant, a release agent, and a modified layered inorganic material in which at least part of interlayer ions is modified with an organic ion, wherein the toner includes the release agent in an amount of from 3 to 6% by weight based on the total weight of the toner, and concentration of the modified layered inorganic material in a surface portion of the toner is greater than the average concentration thereof in the toner, and wherein the toner is subjected to FTIR-ATR, the ratio (P2850/P828) of the strength of the peak at 2850 cm−1 to that of the peak at 828 cm−1, is from 0.03 to 0.10. An image forming apparatus and a process cartridge which form a toner image using the toner.
摘要:
A toner including a binder resin, a colorant, and a release agent is provided. The difference in absorbance ratio between the toner heated for 1 minute in an atmosphere of 100° C. and the toner stored in an atmosphere of 23° C. is from 0.1 to 0.2. The absorbance ratio is a ratio of an absorbance specific to the release agent (such as at 2850 cm−1 for a wax) to an absorbance specific to the binder resin (such as at 828 cm−1 for a polyester based binder resin), as measured by a Fourier transform infrared-total reflectance (FTIR-ATR) method.
摘要:
To provide a toner containing an ethyl acetate-soluble polyester component and an ethyl acetate-insoluble polyester component, wherein the toner is granulated in an aqueous medium, the ethyl acetate-insoluble polyester component is obtained by elongating and/or cross-linking a modified polyester resin during granulating and/or after granulating, the modified polyester resin is produced by condensation polymerization of an acid component and at least one type of diol compound selected from aliphatic diol and alicyclic diol in the presence of a catalyst, and the mass average molecular weight of the modified polyester resin is 10,000 to 100,000.
摘要:
A toner containing a toner particle manufactured by dispersing an organic solvent in which a component comprising a polymer having a portion reactive with an active hydrogen group is dispersed or dissolved in an aqueous medium; and reacting the polymer with a compound having at least one active hydrogen group, where the polymer is prepared by reacting an aliphatic polyol, a polyester resin and a diisocyanate compound and has an isocyanate group on at least one end of the polymer.
摘要:
To provide a toner (X), which contains toner particles, each toner particle contains: a core phase (Q) containing a crystalline resin (A); and a shell phase (S) provided on a surface of the core phase (Q), where the shell phase (S) contains a crystalline polyurethane resin (B), wherein maximum peak temperature (Ta) of heat of melting of the crystalline resin (A) is 40° C. to 70° C., and maximum peak temperature (Tu) of heat of melting of the crystalline polyurethane resin (B) is 50° C. to 90° C.
摘要:
An electrophotographic toner, including: a binder resin; a colorant; and an organically-modified layered inorganic mineral, wherein the binder resin contains 50% by mass or more of a crystalline resin relative to the binder resin, and the crystalline resin contains a resin having a sulfonic acid group, and wherein an amount of the sulfonic acid group is 0.1% by mass to 2.0% by mass relative to the resin having the sulfonic acid group.
摘要:
A toner including: a binder resin; and a colorant, wherein the toner is obtained by dispersing or emulsifying an oil phase in an aqueous solvent containing an organic sulfonic acid salt and an inorganic salt, the oil phase including the binder resin and the colorant dissolved or dispersed in an organic solvent, wherein the binder resin comprises a crystalline resin in an amount of 50% by mass or more relative to the binder resin, and wherein the toner has an average circularity of 0.980 or less.
摘要:
A toner for developing an electrostatic image is provided. The toner includes at least a binder resin; a colorant; and a particulate release agent. The particulate release agent is prepared by heating the release agent to a temperature not lower than a melting point of the release agent to melt the release agent, dissolving the melted release agent in a supercritical fluid or a sub-critical fluid, and feeding the solution into a liquid so that the solution is depressurized and the particulate release agent is formed in the liquid.
摘要:
Toner contains a binder resin containing two or more kinds of crystalline resins; and a coloring agent, wherein the two or more kinds of crystalline resins have at least two endothermic peak temperatures in a set of endothermic peak temperatures of the two or more kinds of crystalline resins as measured by differential scanning calorimetry (DSC).
摘要:
A toner including a colorant and a first binder resin is provided. The first binder resin has first and second glass transition points at a temperature Tg1 of −20 to 20° C. and a temperature Tg2 of 35 to 65° C., respectively, measured by a differential scanning calorimeter at a heating rate of 5° C./min. A ratio h1/h2 of a baseline displacement h1 observed in the first glass transition point to a baseline displacement h2 observed in the second glass transition point is less than 1.0. The first binder resin has a structure in which a first phase is dispersed in a second phase. The first and second phases consist of portions having larger and smaller phase difference values, respectively, than an intermediate value between maximum and minimum phase difference values in a binarized phase image obtained by an atomic force microscope with a tapping mode method.