摘要:
The present invention relates to dental materials composed of calix[n]arenes and also to the use thereof for cements, composites, adhesives and coating materials in the dental field. The materials include (a) 0.5 to 90% by weight of at least one polymerizable calix[n]arene according to formula (I), (b) 0.01 to 5% by weight of initiator, (c) 0 to 90% by weight of at least one additional monomer which can polymerize under cationic and/or radical conditions and/or which can polymerize by ring opening, (d) 0 to 85% by weight of filler, (e) 0.01 to 5% by weight of additive and (f) 0 to 70% by weight of solvent.
摘要:
The present invention relates to dental materials composed of calix[n]arenes and also to the use thereof for cements, composites, adhesives and coating materials in the dental field. The materials include (a) 0.5 to 90% by weight of at least one polymerizable calix[n]arene according to formula (I), (b) 0.01 to 5% by weight of initiator, (c) 0 to 90% by weight of at least one additional monomer which can polymerize under cationic and/or radical conditions and/or which can polymerize by ring opening, (d) 0 to 85% by weight of filler, (e) 0.01 to 5% by weight of additive and (f) 0 to 70% by weight of solvent.
摘要:
The present invention relates to dental materials composed of calix[n]arenes and also to the use thereof for cements, composites, adhesives and coating materials in the dental field. The materials include (a) 0.5 to 90% by weight of at least one polymerizable calix[n]arene according to formula (I), (b) 0.01 to 5% by weight of initiator, (c) 0 to 90% by weight of at least one additional monomer which can polymerize under cationic and/or radical conditions and/or which can polymerize by ring opening, (d) 0 to 85% by weight of filler, (e) 0.01 to 5% by weight of additive and (f) 0 to 70% by weight of solvent.
摘要:
Dental composite materials based on (meth)acrylate, exhibiting a proportion of TCD monomers in the total composition of 1-15% by weight and the quotient of flexural strength/shrinkage tension is at least 35.
摘要:
Compositions for dental composites comprisingmonomers, crosslinking agents, fillers, initiators, A the proportion of crosslinking agent being formed in an amount of more than 50% by acrylate monomers with a TCD urethane structure having the general formula in which A, X, Z, R1 R2 R3 and r have the meaning indicated in claim 1, provide polymerized composite materials with a particularly low cytotoxicity according to the standard requirements according to ISO 10993-5 and DIN EN ISO 7405.
摘要翻译:包含单体,交联剂,填料,引发剂的牙科复合材料的组合物A通过具有以下通式的TCD氨基甲酸酯结构的丙烯酸酯单体形成的交联剂的比例大于50%,其中A,X,Z, R1R2 R3和r具有权利要求1所述的含义,根据ISO 10993-5和DIN EN ISO 7405的标准要求,提供具有特别低的细胞毒性的聚合复合材料。
摘要:
Dental composites comprising monomers, crosslinking agents, fillers, and initiators, in which the crosslinking agent comprises more than 50% by weight of the acrylate monomer TCD-DI-HEA, and the cyctotoxicity of the cured composite as determined according to the standard requirements of ISO 10993-5 and DIN EN ISO 7405 is assessed into the category “no cytotoxic potential”.
摘要翻译:包含单体,交联剂,填料和引发剂的牙科复合材料,其中交联剂包含大于50重量%的丙烯酸酯单体TCD-DI-HEA,以及根据标准要求确定的固化复合物的细胞毒性 ISO 10993-5和DIN EN ISO 7405被评估为“无细胞毒性潜力”类别。
摘要:
Dental composite materials based on (meth)acrylate, exhibiting a proportion of TCD monomers in the total composition of 1-15% by weight and the quotient of flexural strength/shrinkage tension is at least 35.
摘要:
Among other things, a silicone composition curing by condensation at room temperature is prepared from a base dough containing filler and polyorganosiloxane having hydroxy groups, as well as from an activator component containing crosslinker and a catalyst of an organometallic compound, which is characterized in that the activator component additionally contains a polyether having at most one alkoxysilyl group and/or a polyaddition product based on polyether and having at most one alkoxysilyl group.
摘要:
The present invention relates to molding compositions based on silane-terminated polyether derivatives, to a process for their preparation and to their use.
摘要:
Dynamic mixer for viscous pastes, having a buffer chamber for receiving multiple components and having no separation between buffer chamber and mixing chamber.