摘要:
The present invention relates to electrically conductive devices comprising at least one electrically conductive substrate surrounded by an interpolymer composition. The interpolymer composition comprises at least one substantially random interpolymer comprising: (i) polymer units derived from: (a) at least one vinyl or vinylidene aromatic monomer, or (b) at least one hindered aliphatic or cycloaliphatic vinyl or vinylidene monomer; or (c) a combination of at least on vinyl or vinylidene aromatic monomer and at least one hindered aliphatic or cycloaliphatic vinyl or vinylidene monomer; and (ii) polymer units derived from at least one aliphatic olefin monomer having from about 2 to about 20 carbon atoms. Such devices include, for example, wire and cable assemblies.
摘要:
The present invention relates to compositions having enhanced ignition resistance, comprising: (A) from about 5 to about 90 percent by weight of at least one substantially random interpolymer; (B) from about 10 to about 94.9 percent by weight of at least one filler selected from ammonium polyphosphate, magnesium hydroxide, calcium hydroxide, and aluminum trihydrate; and (C) at least one component selected from; (1) about 5 to about 50 percent by weight of at least one filler; or (2) about 0.5 to about 20 percent by weight of at least one metal borate, and, optionally, about 0.5 to about 10 percent by weight of at least one processing aid; or (3) about 0.1 to about 15 percent by weight of at least one initiator or at least one coupling agent; or (4) about 0.1 to about 20 percent by weight of at least one hindered amine stabilizer.
摘要:
The present invention is at least a two-component thermoplastic elastomeric composition comprising at least one block copolymer wherein the composition has essentially the same comparative elasticity, high temperature serviceability and hardness as the unmodified, undiluted (neat) block copolymer portion of the composition. The composition also shows enhanced thermal stability and processibility and is well suited for fabricating elastic moldings, films and fibers as well as for formulating with asphalts, adhesives and sealants. The novel thermoplastic elastomeric composition comprises (a) from about 50 to about 99 percent by weight of at least one block copolymer and (b) about 1 to about 50 percent by weight of at least one ethylene interpolymer having a density from about 0.855 g/cc to about 0.905 g/cc, wherein the ethylene interpolymer in the amount employed is a substantially inert extender of the block copolymer and the composition is further characterized as having: i. storage moduli throughout the range of −26° C. to 24° C. of less than about 3.5×109 dynes/cm2, ii. a ratio of storage modulus at −26° C. to storage modulus at 24° C. of less than about 4, and iii. storage moduli at −26° C. and 24° C. about 0.2 to about 3 times higher than the storage moduli at −26° C. and 24° C., respectively, of the neat block copolymer portion of the composition.
摘要:
Filled thermoplastic compositions useful e.g., as sound-deadening sheeting for automotive carpet are obtained by blending at least one ethylene/&agr;-olefin interpolymer; about 40-95 percent by weight of filler; and optionally elastomeric polymers.
摘要:
The present invention is at least a two-component thermoplastic elastomeric composition comprising at least one block copolymer wherein the composition has essentially the same comparative elasticity, high temperature serviceability and hardness as the unmodified, undiluted (neat) block copolymer portion of the composition. The composition also shows enhanced thermal stability and processibility and is well suited for fabricating elastic moldings, films and fibers as well as for formulating with asphalts, adhesives and sealants. The novel thermoplastic elastomeric composition comprises (a) from about 50 to about 99 percent by weight of at least one block copolymer and (b) about 1 to about 50 percent by weight of at least one ethylene interpolymer having a density from about 0.855 g/cc to about 0.905 g/cc, wherein the ethylene interpolymer in the amount employed is a substantially inert extender of the block copolymer and the composition is further characterized as having: i. storage moduli throughout the range of −26° C. to 24° C. of less than about 3.5×109 dynes/cm2, ii. a ratio of storage modulus at −26° C. to storage modulus at 24° C. of less than about 4, and iii. storage moduli at −26° C. and 24° C. about 0.2 to about 3 times higher than the storage moduli at −26° C. and 24° C., respectively, of the neat block copolymer portion of the composition.
摘要:
A thermoplastic elastomeric blend composition comprising: A) from 99 to 1 weight percent of an elastomer block copolymer comprising at least one segment of a styrenic polymer and at least one segment of an elastomeric saturated olefin polymer; and B) from 1 to 99 weight percent of a linear or substantially linear ethylene/&agr;-olefin interpolymer, and fabricated articles made from such composition.
摘要:
A thermoplastic elastomeric blend composition comprising: A) from 99 to 1 weight percent of an elastomer block copolymer comprising at least one segment of a styrenic polymer and at least one segment of an elastomeric saturated olefin polymer; and B) from 1 to 99 weight percent of a linear or substantially linear ethylene/&agr;-olefin interpolymer, and fabricated articles made from such composition.
摘要:
The present invention is at least a two-component thermoplastic elastomeric composition comprising at least one block copolymer wherein the composition has essentially the same comparative elasticity, high temperature serviceability and hardness as the unmodified, undiluted (neat) block copolymer portion of the composition. The composition also shows enhanced thermal stability and processibility and is well suited for fabricating elastic moldings, films and fibers as well as for formulating with asphalts, adhesives and sealants. The novel thermoplastic elastomeric composition comprises (a) from about 50 to about 99 percent by weight of at least one block copolymer and (b) about 1 to about 50 percent by weight of at least one ethylene interpolymer having a density from about 0.855 g/cc to about 0.905 g/cc, wherein the ethylene interpolymer in the amount employed is a substantially inert extender of the block copolymer and the composition is further characterized as having: i. storage moduli throughout the range of −26° C. to 24° C. of less than about 3.5×109 dynes/cm2, ii. a ratio of storage modulus at −26° C. to storage modulus at 24° C. of less than about 4, and iii. storage moduli at −26° C. and 24° C. about 0.2 to about 3 times higher than the storage moduli at −26° C. and 24° C., respectively, of the neat block copolymer portion of the composition.
摘要:
Filled compositions having good low temperature impact performance made from a thermoplastic (e.g., a polyolefin such as polypropylene) and either at least one linear ethylene/C.sub.5 -C.sub.20 .alpha.-olefin or at least one substantially linear ethylene/C.sub.3 -C.sub.20 .alpha.-olefin polymer are disclosed. The compositions are easily molded and have particular utility in making automotive facia, parts and other household articles.
摘要翻译:由热塑性塑料(例如,聚烯烃如聚丙烯)和至少一种直链乙烯/ C5-C20α-烯烃或至少一种基本上线性的乙烯/ C 3 -C 20α-烯烃聚合物制成的具有良好低温冲击性能的填充组合物 被披露。 组合物易于模塑,并且在制造汽车面板,零件和其它家用制品方面具有特别的用途。
摘要:
Filled compositions having good low temperature impact performance made from a thermoplastic (e.g., a polyolefin such as polypropylene) and either at least one linear ethylene/C.sub.5 -C.sub.20 .alpha.-olefin or at least one substantially linear ethylene/C.sub.3 -C.sub.20 .alpha.-olefin polymer are disclosed. The compositions are easily molded and have particular utility in making automotive facia, parts and other household articles.