摘要:
A process has been surprisingly discovered that can produce a high heat carbonate polymer (i.e., one with a Tg greater that 150.degree. C.), without the drawbacks encountered in attempts to produce a high heat carbonate polymer. The process of the instant invention comprises the steps of:(1) reacting an aromatic amine with a dihydric phenol to prepare an aminophenol;(2) reacting an anhydride or dianhydride with the aminophenol to prepare a phenolic precursor; and(3) reacting the phenolic precursor with a carbonate precursor to prepare a high heat carbonate polymer.
摘要:
An anti-static thermoplastic resin composition of 90-99.95 weight % of a thermoplastic resin and correspondingly 10 to 0.05 weight % of a halogenated carbon sulfonic acid salt of a polysubstituted phosphonium compound such as a fluorinated phosphonium sulfonate and wherein the thermoplastic resin is either an aromatic polycarbonate, polyetherimide, polyester, polyphenylene ether, polyphenylene ether/styrene polymer blend, polyamide, polyketone, acrylonitrile-butadiene-styrene, blends thereof and blends thereof with other materials. Preferably the thermoplastic resin is a transparent aromatic polycarbonate.
摘要:
An anti-static thermoplastic resin composition of 90-99.95 weight % of a thermoplastic resin and correspondingly 10 to 0.05 weight % of a halogenated carbon sulfonic acid salt of a polysubstituted phosphonium compound such as a fluorinated phosphonium sulfonate and wherein the thermoplastic resin is either an aromatic polycarbonate, polyetherimide, polyester, polyphenylene ether, polyphenylene ether/styrene polymer blend, polyamide, polyketone, acrylonitrile-butadiene-styrene, blends thereof and blends thereof with other materials. Preferably the thermoplastic resin is a transparent aromatic polycarbonate.
摘要:
The disclosure describes reacting a multi-functional phenolic or carboxylic branching agent with a transesterification catalyst to form an organic salt prior to reactive extrusion of said organic salt branching agent with linear polycarbonate resin as a means to dramatically increase the efficiency of the branching agent in the preparation of branched polycarbonate.
摘要:
Polycarbonate compositions comprising copolymers of bis-(4-hydroxyphenyl)methane and 2,2-bis-(4-hydroxyphenyl)propane are described and they unexpectedly display high glass transition temperatures, high impact resistances, flame retardant properties and superior brittle ductile transition temperature.
摘要:
The present invention provides a composition comprising polycarbonate wherein the polycarbonate has a very low Fries content (e.g., above 5 ppm and below 360 ppm). The present invention also provides a polycarbonate having a very low Fries content which is made by the melt process. This polycarbonate has high ductility and high impact strength. The invention also provides a method for making these compositions. Another aspect of the invention is an optical disk comprising polycarbonate having a very low Fries content which is made by the melt process. Such optical disks resist breakage due to bending.
摘要:
Increasing the endcap level to a level greater than about 90% for Optical Quality (OQ) Melt Polycarbonate significantly reduces the as-molded static charge for injection molded parts for Optical Disc applications. The use of resins with higher endcap levels in combination with antistatic additives provides a highly robust formulation suitable for even the most demanding emerging formats as Digital Versatile Disc (DVD) and in all commercial Optical media molding machines. Thus, optical quality polycarbonates are prepared by performing a base-catalyzed polymerization of a diaryl carbonate and a dihydric phenol under conditions effective to produce a polycarbonate product having an endcap level of 90% or greater.
摘要:
The weight average molecular weight of a polycarbonate resin is predictably reduced by reaction with a multifunctional aliphatic compound at a temperature of 250 C. to 350 C.
摘要:
The invention relates to polymer mixtures which comprise a polyphenylene ether, a polyoctenylene and TiO.sub.2 or BaSO.sub.4. The presence of TiO.sub.2 or BaSO.sub.4 leads to an improvement of the mechanical properties.
摘要翻译:本发明涉及包含聚苯醚,聚辛烯和TiO 2或BaSO 4的聚合物混合物。 TiO 2或BaSO 4的存在导致机械性能的改善。
摘要:
Increasing the endcap level to a level greater than about 90% for Optical Quality (OQ) Melt Polycarbonate significantly reduces the as-molded static charge for injection molded parts for Optical Disc applications. The use of resins with higher endcap levels in combination with antistatic additives provides a highly robust formulation suitable for even the most demanding emerging formats as Digital Versatile Disc (DVD) and in all commercial Optical media molding machines. Thus, optical quality polycarbonates are prepared by performing a base-catalyzed polymerization of a diaryl carbonate and a dihydric phenol under conditions effective to produce a polycarbonate product having an endcap level of 90% or greater.