摘要:
A composition, including a polymer binder resin A, a UV-curing acrylate B, a heat curing agent C, and a photopolymerization initiator D. The composition includes about 20 to about 150 parts by weight of the UV-curing acrylate B per 100 parts by weight of the polymer binder resin A, and the UV-curing acrylate B is a solid or near-solid at room temperature and has a viscosity of about 10,000 cps or more at 40° C.
摘要:
An adhesive composition and an optical member using the same, the adhesive composition including about 100 parts by weight of a (meth)acrylate copolymer including repeating units derived from a C1-20 alkyl(meth)acrylate monomer, an aromatic group-containing monomer, and a carboxyl group-containing monomer; about 0.01 to about 10 parts by weight of a crosslinking agent; about 0.01 to about 5 parts by weight of a silane coupling agent; and about 0.01 to about 5 parts by weight of a crosslinking catalyst.
摘要:
An adhesive composition and an optical member using the same, the adhesive composition providing an adhesive having a storage modulus of about 8×105 to about 1×108 dyne/cm2 and a gel fraction of about 83% to about 95% as defined by Equation 1: Gel fraction (%)=(A/B)×100, [Equation 1] in Equation 1, A is a mass measured after dissolving the adhesive at 23° C. for 48 hours in a solvent and then drying for 24 hours, and B is an initial mass.
摘要翻译:粘合剂组合物和使用其的光学构件,所述粘合剂组合物提供具有约8×10 5至约1×10 8达因/ cm 2的储能模量和约83%至约95%的凝胶分数的粘合剂,如式 1:凝胶分数(%)=(A / B)×100,等式1中的[等式1],A是在粘合剂在23℃下在溶剂中溶解48小时后,然后干燥24小时时测量的质量 ,B为初始质量。
摘要:
An adhesive composition and an optical member using the same, the adhesive composition providing an adhesive having a storage modulus of about 8×105 to about 1×108 dyne/cm2 and a gel fraction of about 83% to about 95% as defined by Equation 1: Gel fraction (%)=(A/B)×100, [Equation 1] in Equation 1, A is a mass measured after dissolving the adhesive at 23° C. for 48 hours in a solvent and then drying for 24 hours, and B is an initial mass.
摘要:
An adhesive composition and an optical member using the same, the adhesive composition including about 100 parts by weight of a (meth)acrylate copolymer including repeating units derived from a C1-20 alkyl (meth)acrylate monomer, an aromatic group-containing monomer, and a carboxyl group-containing monomer; about 0.01 to about 10 parts by weight of a crosslinking agent; about 0.01 to about 5 parts by weight of a silane coupling agent; and about 0.01 to about 5 parts by weight of a crosslinking catalyst.
摘要:
An adhesive composition and an optical member using the same, the adhesive composition including an acrylic resin; an isocyanate cross-linking agent; and a carbodiimide cross-linking agent, wherein the adhesive composition exhibits a creeping distance of about 100 μm or less when the composition attached to a glass substrate with a bonding area of about 1.5 cm×1.5 cm is left at about 22° C. and about 50% RH for about 3 days and is subjected to a load of about 10 gf/mm2 for about 1,000 seconds, and a storage modulus of about 1×105 to about 1×107 Pa at about 10 Hz and about 30° C. under conditions in which a sample has a thickness of about 1 mm and an elongation of about 10%.