The invention discloses a rolling method for producing a copper clad aluminum row, which comprises the following steps: 1, selecting a copper pipe with uniform wall thickness and an aluminum bar in transition fit with the inner wall of the copper pipe, and cleaning the copper pipe and the aluminum bar to remove oil stains and oxidation layers; 2, pressing the aluminum bar into the copper pipe to form a composite blank, and plugging two ends of the composite blank tightly; 3, heating the composite blank to between 300 and 540 DEG C, preserving the heat for 30 to 60 minutes, then thermally rolling the composite blank for 1 to 3 times, and coldly rolling the composite blank for 1 to 4 times; 4, straightening and acid-washing a rolled product; 5, carrying out diffusion treatment at the temperature of between 200 and 550 DEG C under the protection of nitrogen of one atmospheric pressure, and preserving the heat for 1 to 3 hours; and 6, drawing the treated product to form a final product. The rolling method for producing the copper clad aluminum row not only has short process flow and high production efficiency, but also can save limited resources and reduce the cost.