CN103275606A 含磷醇酸树脂防火磁漆及其制备方法 失效 - 权利终止

含磷醇酸树脂防火磁漆及其制备方法
摘要：
含磷醇酸树脂防火磁漆及其制备方法，按质量百分数计，含磷醇酸树脂配方为：含磷醇酸树脂35%~43%，颜料20%~23%，三氧化二钼1%~1.2%，二甲基硅油0.1%~0.12%，催干剂0.9%~1.08%，溶剂35%~42%；其制备步骤为：将配方量溶剂、颜料、三氧化二钼依次加入多用分散研磨机中进行高速分散30～60min，降低搅拌速度加入含磷醇酸树脂再分散20～40min，加入二甲基硅油，用锥形磨研磨至所需的细度，然后在多用分散研磨机中分散10～20min后加入催干剂分散均匀即得产品。
摘要（英）：

The invention discloses phosphorous alkyd resin fireproof enamel paint and a preparation method thereof. A formula of the phosphorous alkyd resin fireproof enamel paint comprises the following materials in percentage by weight: 35%-43% of phosphorous alkyd resin, 20%-23% of pigment, 1%-1.2% of molybdenum sesquioxide, 0.1%-0.12% of simethicone, 0.9%-1.08% of drier and 35%-42% of solvent. The preparation method of the enamel paint comprises the following steps that the solvent, the pigment and molybdenum sesquioxide at the formula ratio are sequentially added to a multipurpose dispersion and grinding machine to be dispersed at a high speed for 30-60min and re-dispersed for 20-40mina after a stirring speed is reduced and the phosphorous alkyd resin is added; simethicone is added, ground by a cone mill to the required fineness, and dispersed in the multipurpose dispersion and grinding machine for 10-20min; then the drier is added, and dispersed uniformly; and the enamel paint is obtained.

公开/授权文献
0/0