CN104789059A 一种彩色路用涂料 有权

一种彩色路用涂料
摘要：
一种彩色路用涂料，是由下列重量配比的原材料制得：双酚A型环氧树脂10～30份，阴离子水性苯丙乳液15~40份，丙二醇12～18份，有机膨润土3～12份，硫酸钡5～10份，色浆5～10份，去离子水20～45份。本发明彩色路用涂料是可涂染于水泥混凝土路面和沥青路面的一种颜色鲜艳而又耐磨耐候的高分子材料，依照本发明所制得的彩色路用涂料具有耐磨耐候性能优异、耐腐蚀性强、黏附性能强、成本低的特点，其拉拔值≥5.9Pa、磨耗值≤18%、黏附性≥2.9Mpa，收率高达99%以上，本发明制备工艺简单，产量大，成本低，适合工业化生产。
摘要（英）：

The invention relates to a paint for colored roads, which is prepared from the following raw materials in parts by weight: 10-30 parts of bisphenol A epoxy resin, 15-40 parts of anionic water-based styrene-acrylic emulsion, 12-18 parts of propanediol, 3-12 parts of organobentonite, 5-10 parts of barium sulfate, 5-10 parts of color paste and 20-45 parts of deionized water. The paint for colored roads is a bright-color wear-resistant weather-resistant high polymer material applicable to a cement concrete pavement and an asphalt pavement. The paint for colored roads has the characteristics of excellent wear resistance, excellent weather resistance, high corrosion resistance, high adhesion performance and low cost. The drawing value is greater than or equal to 5.9 Pa, the wear value is less than or equal to 18%, the adhesion performance is greater than or equal to 2.9 MPa, and the high yield is up to 99% above. The paint for colored roads has the advantages of simple preparation technique, high yield and low cost, and is suitable for industrial production.

公开/授权文献
0/0