The invention discloses a high adhesive force building aluminum template powder coating which is prepared from the following components: matrix resin, a curing agent, filler, a lyophobic auxiliary agent, low melting point alloy powder, a metal corrosion inhibitor, an epoxy polymerization inhibitor/retarding agent, a universal auxiliary agent, a silane coupling agent and pigments. The coating is high in adhesive force, and the surface hardness reaches 5-6H; the surface of the coating is strongly lyophobic, and the lyophobic angle can reach 90 degrees or above; adhesion of concrete motor and a coating is reduced, and the coating does not fall if being cycled for 50 period or more at a single time, so that the coating fully can meet cyclic use of a project; the coating is highly strong in alkali resistance, does not fall and crack if being soaked for 1200h in constant alkali-resistant water (PH=12) and still has a good adhesive force; and the coating is damp and wet resistant, high in surface hardness, easy to demold and low in cyclic cost among projects. The cyclic period can reach 20 years or above if the metal surface coating is re-sprayed after being polished. The coating is easily constructed by a worker, high in universality, high in surface evenness, wide in source and easy to process.