CN108951123A 一种真丝织物的初炼工艺 无效 - 撤回

一种真丝织物的初炼工艺
摘要：
本发明公开了一种真丝织物的初炼工艺，其特征在于：首先，调制初炼溶液，按以下质量份数进行，用5吨热水的初炼缸,加入分散剂16‑20kg、纯碱4‑5kg、泡化碱4‑6kg、保险粉1‑1.5kg,混合均匀后，用星形架将真丝织物挂起来，然后将真丝织物浸入到初炼缸中，随后加温，温度控制在96‑98度，炼90‑100分钟，将星形架吊出，使真丝织物在空气中冷却到55‑60度，然后放入25‑27度水中漂洗干净。该真丝织物的初炼工艺可方便快速脱丝胶，对环境友好。
摘要（英）：

The invention discloses a primary refining process of a real silk fabric. The primary refining process is characterized by comprising the steps of preparing a primary refining solution in parts by mass: adding 16kg-20kg of a dispersing agent, 4kg-5kg of sodium carbonate, 4kg-6kg of sodium silicate and 1kg-1.5kg of sodium hydrosulfite into a primary refining cylinder filled with 5t hot water, uniformly mixing, hanging the real silk fabric with a star frame, dipping the real silk fabric into the primary refining cylinder, heating, carrying out refining at 96-98 DEG C for 90-100 minutes, hoistingthe star frame out, cooling the real silk fabric to 55-60 DEG C in air, putting the real silk fabric into water with a temperature of 25-27 DEG C, and completely rinsing. According to the primary refining process, sericin can be conveniently and rapidly removed; and the primary refining process is environment-friendly.

0/0