The invention discloses a single-faced real silk pearl forging whitening process. The process comprises the following steps: 1) preparing the amount of single-faced real silk pearl forging billets according to an operation card, saddling and nailing loops; 2) degumming and whitening: soaking in a 5-ton cold water tank for 40-60 minutes under the temperature at 15-30 DEG C, using a 5-ton water primary melting tank, adding 16-20KG dispersing agent, 4-5kg sodium carbonate, 4-6kg sodium silicate and 1-1.5kg sodium hydrosulfite, starting to put into the single-faced real silk pearl forging billetswhen the water temperature is at 80-85 DEG C, rising temperature to 96-98 DEG C and then forging for 40-50 minutes, slowly retracting the twisted silk fabrics in the forging process, and starting to degum when the water temperature is at 96-98 DEG C. According to the single-faced real silk pearl forging whitening process, the shrinkage rate is increased while degumming and whitening are performed,so that the concavo-convex sense of pearl texture can be highlighted.