CN109810631A 水性有机硅溶胶涂料及其制备方法和制品 无效 - 驳回

水性有机硅溶胶涂料及其制备方法和制品
摘要：
本发明涉及一种水性有机硅溶胶涂料及其制备方法和制品，其中，水性有机硅溶胶涂料，按重量份计，包括如下原料组分：水性有机硅溶液85～95份、硅烷改性没食子酸1～5份、缓蚀剂0.1～1份、增稠剂0.5～2份、防锈颜料2～6份和消泡剂0.3～1份。该水性有机硅胶涂料具有优良的带锈涂装性能，可以实现带锈涂装，从而降低钢、铁结构表面处理要求；且具有极强的附着性能及防腐、防锈性能，具有广泛的应用前景。
摘要（英）：

The invention relates to water-based organosilicon sol coating, a preparation method thereof and a product. The water-based organosilicon sol coating is prepared from the following raw material components in parts by weight: 85-95 parts of a water-based organosilicon solution, 1-5 parts of silane modified gallic acid, 0.1-1 part of a corrosion inhibitor, 0.5-2 parts of a thickener, 2-6 parts of anti-rust pigment and 0.3-1 part of a defoamer. The water-based organosilicon sol coating has excellent on-rust coating performance, on-rust coating can be realized, and thus the surface treatment requirement of steel and iron structures is lowered; and the water-based organosilicon sol coating has quite high adhesion performance, anti-corrosion performance and anti-rust performance, and has wide application prospects.

0/0