There is provided a thick steel plate having good multipass weld joint CTOD characteristics for low to medium heat input and a method for manufacturing the thick steel plate. A steel plate containing, on a mass percent basis, C: 0.03% to 0.12%, Si: 0.5% or less, Mn: 1.0% to 2.0%, P: 0.015% or less, S: 0.0005% to 0.0050%, Al: 0.005% to 0.060%, Ni: 0.5% to 2.0%, Ti: 0.005% to 0.030%, N: 0.0015% to 0.0065%, O: 0.0010% to 0.0050%, Ca: 0.0005% to 0.0060%, and optionally one or two or more of Cu and the like, wherein Ti/N, Ceq, Pcm, and ACR are in particular ranges, a base material of the plate has an effective grain size of 20 μm or less at half the thickness of the plate, and the plate contains a particular number of complex inclusions at ¼ and ½ of the thickness of the plate, the complex inclusions being composed of a sulfide containing Ca and Mn and an oxide containing Al and having an equivalent circular diameter of 0.1 μm or more. Steel having the composition described above is heated at a particular temperature, is then hot-rolled, and is cooled.