An object of the invention is to provide a coated cutting tool whose tool life can be extended by having excellent wear resistance and fracture resistance. The coated cutting tool includes: a substrate; and a coating layer formed on a surface of the substrate, in which the coating layer includes a lower layer, an intermediate layer, and an upper layer in this order from a substrate side to a surface side of the coating layer, the lower layer includes one or more Ti compound layers formed of a specific Ti compound, the intermediate layer contains TiCNO, TiCO, or TiAlCNO, the upper layer contains α-type Al2O3, an average thickness of the lower layer is 2.0 μm or more and 8.0 μm or less, an average thickness of the intermediate layer is 0.5 μm or more and 2.0 μm or less and is 10% or more and 20% or less of a thickness of the entire coating layer, an average thickness of the upper layer is 0.8 μm or more and 6.0 μm or less, and in the intermediate layer, a ratio of a length of CSL grain boundaries to a total length 100% of a total grain boundary is 20% or more and 60% or less.