US20050193861A1 Iron-based sintered alloy material for valve seat 失效
用于阀座的铁基烧结合金材料

Iron-based sintered alloy material for valve seat
摘要:
An iron-based sintered alloy material for a valve seat having improved wear resistance and reduced opposite aggressibility to a mating valve. The iron-based sintered alloy material contains 10% to 20% by area of first hard particles and 15% to 35% by area of second hard particles dispersed in a base matrix phase, the first and the second hard particles accounting for 25% to 55% by area in total. The first hard particles are composed of a cobalt-based intermetallic compound and have a size of 10 to 150 μm and a hardness of at least 500HV0.1 and less than 800HV0.1. The second hard particles are composed of a cobalt-based intermetallic compound and have a size of 10 to 150 μm and a hardness of at least 800HV0.1 and less than 1100HV0.1. Solid lubricant particles may also be dispersed in the base matrix phase.