In a method of manufacturing a grain-oriented electrical steel sheet including a nitriding treatment (step S7) and adopting so-called “low-temperature slab heating”, the finish temperature of finish rolling in hot rolling (step S2) is set to 950° C. or below, the cooling is started within 2 seconds after completion of the finish rolling, and a steel strip is coiled at 700° C. or below. The cooling rate over the duration from the end of finish rolling to the start of coiling is set to 10° C./sec or above. In annealing (step S3) of the hot-rolled steel strip, the heating rate in the temperature range from 800° C. to 1000° C. is set to 5° C./sec or above.