A weld repair for repairing an imperfection in a nickel base superalloy article. The weld repair provides a weldment that includes a weld joint, a heat affected zone adjacent to the weld joint and a nickel base alloy base material adjacent to the heat affected zone and opposite the weld joint. The weld joint utilizes a nickel base weld filler material, having a composition, in weight percent of 0.03-0.13% C, 22.0-23.0% Cr, 18.5-19.5% Co, 1.8-2.2% W, 0.7-1.4% Nb, 2.2-2.4% Ti, 1.3-2.0% Al, 0.005-0.040% Zr, 0.002-0.008% B, up to 0.15% Mo, up to 0.35% Fe, up to 0.10% Mn, up to 0.10% Cu, up to 0.10% V, up to 0.15% Hf, up to 0.25% Si, and the balance Ni and incidental impurities. The weld filler material is characterized by an absence of Ta.