Methods for press hardening steel alloys comprised of medium-Mn are provided. The press-hardened steel alloy may have an ultimate tensile strength (UTS) of at least 1,700 MPa and a tensile elongation of at least 8%. The press-hardened steel alloy may be formed in two forming steps above the martensitic finish temperature. The press-hardened steel may have a microstructure comprising martensite at greater than or equal to about 80% to less than or equal to about 98% and retained austenite at less than or equal to about 20% to greater than or equal to about 2%.