Provided is a method for producing a β-sialon fluorescent material, comprising preparing a composition containing a silicon nitride that contains aluminium, oxygen, and europium; heat-treating the composition at a temperature in a range of 1300° C. or more and 1600° C. or less to obtain a heat-treated product; subjecting the heat-treated product to a temperature-decrease of from the heat treatment temperature to 1000° C. as a first temperature-decrease step; and subjecting the heat-treated product to a temperature-decrease of from 1000° C. to 400° C. as a second temperature-decrease step. The first temperature-decrease step has a temperature-decrease rate in a range of 1.5° C./min or more and 200° C./min or less, and the second temperature-decrease step has a temperature-decrease rate in a range of 1° C./min or more and 200° C./min or less