The purpose of the present invention is to provide a method for manufacturing a grain-oriented electrical steel sheet, whereby it becomes possible to manufacture a grain-oriented electrical steel sheet having further improved iron loss properties stably. (Solution) According to one aspect of the present invention, a method for manufacturing a grain-oriented electrical steel sheet is provided, the method being characterized by comprising a re-heating step, a hot rolling step, a hot-rolled sheet annealing step, a cold rolling step, a decarburization annealing step and a final annealing step, wherein the decarburization annealing step includes a heating step of heating a cold-rolled sheet from an inlet side temperature T0° C. to a soaking temperature T2° C. and a soaking step of keeping the temperature of the cold-rolled sheet at the soaking temperature T2° C., and the heating rate HR1 from the time point when the temperature of the cold-rolled sheet is an inlet side temperature T0° C. to the time point when the temperature of the cold-rolled sheet reaches a attained temperature T1° C. is 40° C./sec or more and the heating rate HR2 from the time point when the temperature of the cold-rolled sheet is the desired temperature T1° C. to the time point when the temperature of the cold-rolled sheet reaches the soaking temperature T2° C. is more than 15° C./sec to 30° C./sec in the heating in the decarburization annealing step.