A non-oriented electrical steel sheet produced by hot-rolling a steel slab containing Si: 2.8 to 6.5 mass % and Zn: 0.0005 to 0.0050 mass % followed by cold rolling and finish annealing, a coating agent containing at least one element from Sn, Sb, P, S, Se, As, Te, B, Pb, and Bi is applied to the surface after annealing forming an insulation coating with nitriding-suppressing ability. Alternatively, an intermediate layer containing at least one element from Sn, Sb, P, S, Se, As, Te, B, Pb, and Bi and having a nitriding-suppressing ability forms on the steel sheet iron matrix after the annealing and forms an insulation coating, without above elements, on the intermediate layer thus obtaining a non-oriented electrical steel sheet wherein a high strength rotor core with and stator core with excellent magnetic is simultaneously obtained, and a motor core including a stator core and rotor core from the steel sheet.
In a production of a non-oriented electrical steel sheet by hot-rolling a steel slab containing Si: 2.8 to 6.5 mass % and Zn: 0.0005 to 0.0050 mass % followed by cold rolling and finish annealing, a coating agent containing at least one element selected from Sn, Sb, P, S, Se, As, Te, B, Pb, and Bi is applied to the steel sheet surface after the finish annealing to form an insulation coating with a nitriding-suppressing ability. Alternatively, an intermediate layer containing at least one element selected from Sn, Sb, P, S, Se, As, Te, B, Pb, and Bi and having a nitriding-suppressing ability is formed on the steel sheet iron matrix after the finish annealing and form an insulation coating not containing above elements is formed on the intermediate layer thus to obtain a non-oriented electrical steel sheet from which a rotor core with high strength and stator core with excellent magnetic properties after the stress-relief annealing can be obtained at the same time, and a motor core comprising a stator core and rotor core is produced from the steel sheet.