To provide a zirconia perfect sintered body which has a chroma of an excellent color tone and excellent translucency as compared with a zirconia mill blank for dental cutting and machining prepared from a zirconia raw material powder containing various stabilizing materials while maintaining high strength, and does not cause deformation. The zirconia mill blank of the present invention is a semi-fired zirconia mill blank for dental cutting and machining containing a semi-fired body of a ceramic particle, the zirconia mill blank for dental cutting and machining contains zirconium oxide, a stabilizing material consisting of an oxide, and a water-soluble compound salt which contains at least one element selected from calcium, magnesium and a rare earth element and is not an oxide, the content of the stabilizing material in terms of the oxide in the semi-fired body of the ceramic particle is within a range of 2 to 7 mol %, and the content of the water-soluble compound salt in the zirconia mill blank for dental cutting and machining is within a range of 0.1 to 3.5 mol %.