A Polymer compositions that features high degree of toughness, very good processability and extremely high gloss is disclosed. The composition contains (I) a graft rubber polymer obtained by emulsion polymerization of styrene and acrylonitrile in the presence of a mixture of (A) a butadiene polymer latex having a mean particle diameter d50≦250 nm, a particle size distribution width of 20 to 80 nm and a gel content of 30 to 95 wt. %, (B) a butadiene polymer latex with a mean particle diameter d50>250 to 350 nm, a particle size distribution width of 30 to 100 nm and gel content of 30 to 80 wt. %, and (C) a butadiene polymer latex (C) with a mean particle diameter d50>350 nm, a particle size distribution width of 40 to 150 nm, and a gel content of 50 to 95 wt. %. and (II) a rubber-free copolymer of styrene and acrylonitrile. At least one of (A), (B) and (C) is a product of seed polymerization.