Disclosed is a method for making a refractory material from aluminum residues of aluminum recycling. At first, the aluminum residues is mixed with adhesive solution so that the percentage by weight of the adhesive solution is 5 wt % to 10 wt %. The mixture is granulated into grains. The grains are filled in a mold, pressed and then removed from the mold so that the grains are turned into a green body. The green body is heated in a furnace at a range of temperature from 1100° C. to 1400° C. so that the grains are sintered and become a refractory material.