A method for producing an amorphous carbon material for a negative electrode of a lithium-ion secondary battery includes the steps of; pulverizing and classifying a raw coke composition obtained from a heavy-oil composition undergone coking by delayed coking process to obtain powder of the raw coke composition, the raw coke composition having a H/C atomic ratio that is a ratio of hydrogen atoms H and carbon atoms C of 0.30 to 0.50 and having a micro-strength of 7 to 17 mass %; giving compressive stress and shear stress to the powder of the raw coke composition to obtain a carbonized composition precursor; and heating the carbonized composition precursor under an inert atmosphere at a temperature from 900° C. to 1,500° C. so that a size of a crystallite Lc(002) is in a range of 2 nm to 8 nm, the size being calculated from a (002) diffraction line obtained by X-ray wide-angle diffractometry.