A solid polymeric electrolyte having a pattern, and a lithium battery including the same, includes a polymer matrix having a mesh structure and being formed of a cured photo-crosslinking agent; inorganic particles substantially uniformly distributed in the polymer matrix; and a liquid electrolyte comprised of a lithium salt and an organic solvent impregnated between the polymer matrix and the inorganic particles. The liquid electrolyte and the cured photo-crosslinking agent are present in a weight ratio ranging from 50:50 to 99:1. The liquid electrolyte containing the cured photo-crosslinking agent and the inorganic particle are present in a weight ratio ranging from 10:90 to 90:10. The solid polymeric electrolyte has properties suitable for a printing process to provide the pattern including a thickness ranging from about 10 nm to about 500 μm and, prior to curing the photo-crosslinking agent, a viscosity ranging from 100-10,000 poise under a shear rate condition of 1 sec−1.