公开(公告)号：EP2612956A4

公开(公告)日：2015-03-18

申请号：EP11821648

申请日：2011-08-25

申请人： JFE STEEL CORP

发明人： MASUOKA HIROYUKI ,  ANDO SATORU ,  YAMAMOTO SHUNSUKE

IPC分类号： C23G1/08 ,  B21B3/02 ,  C21D9/46 ,  C22C38/00 ,  C22C38/58

CPC分类号： C23G1/085 ,  B21B3/02 ,  C21D8/0205 ,  C21D8/0226 ,  C21D8/0236 ,  C21D8/0273 ,  C21D9/46 ,  C22C38/00 ,  C22C38/001 ,  C22C38/002 ,  C22C38/005 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/12 ,  C22C38/14 ,  C22C38/16 ,  C22C38/22 ,  C22C38/32 ,  C22C38/34 ,  C22C38/38 ,  C23G1/00 ,  C23G1/08 ,  Y10T428/265

公开(公告)号：EP2612957A4

公开(公告)日：2015-04-08

申请号：EP11821649

申请日：2011-08-25

申请人： JFE STEEL CORP

发明人： MASUOKA HIROYUKI ,  ANDO SATORU ,  YAMAMOTO SHUNSUKE

IPC分类号： C23G1/08 ,  B21B3/02 ,  C21D9/46 ,  C22C38/00 ,  C22C38/02 ,  C22C38/58

CPC分类号： C23G1/08 ,  B21B3/02 ,  B21B45/0269 ,  C21D8/0236 ,  C21D8/0278 ,  C22C38/00 ,  C22C38/001 ,  C22C38/002 ,  C22C38/005 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/08 ,  C22C38/12 ,  C22C38/14 ,  C22C38/16 ,  C22C38/22 ,  C22C38/32 ,  C22C38/34 ,  C22C38/38 ,  C23G1/00 ,  C23G1/081 ,  C23G1/085 ,  C23G1/086 ,  C23G1/088 ,  Y10T428/26

摘要： This invention provides a method of producing a cold-rolled steel sheet being excellent in not only the phosphate treatability but also the corrosion resistance after coating under severe corrosion environment such as hot salt water immersion test or composite cycle corrosion test, wherein a continuously annealed steel sheet after cold rolling preferably comprising 0.5-3.0 mass% of Si is pickled to remove a Si-containing oxide layer on a surface layer of the steel sheet and further repickled so that a surface covering ratio of an iron-based oxide on the surface of the steel sheet is not more than 40% and preferably a maximum thickness of the iron-based oxide is not more than 150 nm, as well as a cold-rolled steel sheet produced by this method and a member for automobile using the cold-rolled steel sheet.

摘要翻译： 本发明提供了一种不仅在磷酸盐处理性方面优异的冷轧钢板的制造方法，而且在严酷的腐蚀环境例如热盐水浸渍试验或复合循环腐蚀试验中涂覆后的耐腐蚀性，其中连续退火钢 酸洗后，优选含有0.5〜3.0质量％的Si的片材除去钢板的表面层上的含Si氧化物层，并进一步反复使得表面上的铁基氧化物的表面覆盖率 钢板不超过40％，优选铁基氧化物的最大厚度不大于150nm，以及通过该方法制造的冷轧钢板和使用冷轧的汽车用部件 钢板。