公开(公告)号：EP2927267A1

公开(公告)日：2015-10-07

申请号：EP13857700.2

申请日：2013-11-26

申请人： Mitsubishi Rayon Co., Ltd.

发明人： FUJITA Saki ,  OHTANI Tadashi ,  TAKAHASHI Atsushi ,  FUJIOKA Kiyotoshi

IPC分类号： C08J5/06

CPC分类号： C08J5/24 ,  B32B27/08 ,  B32B27/34 ,  B32B37/06 ,  B32B37/08 ,  B32B37/10 ,  B32B2262/101 ,  B32B2262/106 ,  B32B2305/076 ,  C08J5/042 ,  C08J5/06 ,  C08J2377/00 ,  C08J2377/02 ,  C08J2463/00 ,  C08J2463/02 ,  C08J2475/16 ,  C08K5/053 ,  C08K7/06

摘要： A fiber-reinforced thermoplastic resin prepreg that is a fiber-reinforced polyamide prepreg which contains (A) reinforcing fibers, (B) a sizing agent and (C) a polyamide resin, and wherein the sizing agent (B) and the polyamide resin (C) satisfy the following condition. N m /N 0 m is the average of torques necessary for maintaining the number of revolutions of a roller type blade at 100 rpm/15 minutes, said average representing the fluidity of a mixture, which is obtained by mixing the sizing agent (B) and the polyamide resin (C) at 3:100 (mass ratio), in cases where the mixture is filled into a mixer having the roller type blade and heated and melted at a temperature that is higher than the melting point of the polyamide resin (C) by 30°C.)

摘要翻译： 一种纤维增强热塑性树脂预浸料确实是一种纤维增强聚酰胺预浸其中含有（A）的增强纤维，（B）的上浆剂和（C）的聚酰胺树脂，和worin上浆剂（B）和聚酰胺树脂（ C）满足以下条件。 N×M个/ N 0 <4.0（否是转矩需要：维持辊型叶片的转数为100转/ 15分钟的平均值，所述平均，其中仅表示在箱子的聚酰胺树脂（C）的流动性 聚酰胺树脂（C）被填充到具有踏板型叶片并加热的混合器和在一定温度下熔化，所做的是大于30℃和N米熔点聚酰胺树脂（C）的更高是必要的转矩的平均 用于维持在100rpm / 15分钟辊型叶片的转数，所述平均表示的混合物的流动性，所有这一切是通过在3混合上浆剂（B）和聚酰胺树脂（C）获得：100（ 其中混合物填充到具有踏板型叶片并加热的混合器和在比熔点高的温度下熔化的那样（质量比），在例是聚酰胺树脂C点）由30℃）

公开(公告)号：EP3115503A1

公开(公告)日：2017-01-11

申请号：EP15757853.5

申请日：2015-03-05

申请人： Mitsubishi Rayon Co., Ltd.

发明人： OHTANI Tadashi ,  TAKAHASHI Atsushi ,  FUJITA Saki ,  HARADA Akira

IPC分类号： D06M15/227 ,  C08J5/06 ,  D06M13/17 ,  D06M13/224 ,  D06M15/263 ,  D06M15/347 ,  D06M15/53 ,  D06M15/564 ,  D06M101/40

CPC分类号： C08J5/06 ,  B29B15/122 ,  C08F255/02 ,  C08J5/042 ,  C08J5/24 ,  C08J2300/22 ,  C08J2323/00 ,  C08J2323/12 ,  C08J2377/00 ,  C08J2433/24 ,  C08J2451/06 ,  C08J2471/02 ,  C08K7/06 ,  C08K9/04 ,  C08L23/10 ,  D06M13/17 ,  D06M13/224 ,  D06M15/227 ,  D06M15/263 ,  D06M15/285 ,  D06M15/53 ,  D06M15/564 ,  D06M15/59 ,  D06M2101/40 ,  D06M2200/50 ,  C08F222/06

摘要： A carbon fiber bundle for resin reinforcement, wherein there are adhered by 0.1-5.0 mass% to a carbon fiber bundle in which multiple lengths of filament are bundled, a mixture created by mixing an organic polymer (A) having a mass-average molecular weight of 10000 or more and an organic compound (B) the thermal reduction rate specified in claim 1 of which is 5 mass% or more or an organic compound (B) the thermal reduction rate specified in claim 2 of which is 0.8 mass% or more, the amount of the organic polymer (A) adhered being 0.1 mass% or more.

摘要翻译： 用于树脂增强的碳纤维束，worin存在由0.1-5.0％粘附至按质量计在哪个长丝的多种长度集束的碳纤维束，由有机高分子（A）的混合具有质均分子量创建的混合物 为10,000以上和有机化合物（B）中的所有claimsoft 1中规定的热还原率是5质量％或更多，或有机化合物（B）中的所有claimsoft 2中指定的热还原率是0.8质量％以上的 中，有机聚合物（A）的量附着为0.1质量％以上。

公开(公告)号：EP2924164A1

公开(公告)日：2015-09-30

申请号：EP13856572.6

申请日：2013-11-22

申请人： Mitsubishi Rayon Co., Ltd.

发明人： OHTANI Tadashi ,  KIRIYAMA Takayuki ,  NISHIMOTO Yukio

IPC分类号： D06M15/564 ,  C08J5/06 ,  D06M15/227 ,  D06M15/507 ,  D06M15/55 ,  D06M15/59 ,  D06M101/40

CPC分类号： C08K7/06 ,  B05D1/18 ,  B05D1/28 ,  B05D3/0406 ,  B05D3/12 ,  C08J5/06 ,  C08J5/24 ,  D06M15/227 ,  D06M15/507 ,  D06M15/55 ,  D06M15/564 ,  D06M15/59 ,  D06M2101/40 ,  Y10T428/2918

摘要： Provided are: chopped carbon fiber bundles which have high fluidity without decreasing the dispersibility of carbon fibers and the physical properties of a molded product; and a method for producing chopped carbon fiber bundles with high productivity. Chopped carbon fiber bundles, each of which contain a carbon fiber bundle having a total fineness of from 25,000 dtex to 45,000 dtex (inclusive) and a sizing agent in an amount of from 1% by mass to 5% by mass (inclusive) relative to the total mass of the chopped carbon fiber bundle. The length (L) of each chopped carbon fiber bundle along the fiber direction of the carbon fiber bundle is from 1 mm to 50 mm (inclusive); the ratio of the longest diameter (Dmax) to the shortest diameter (Dmin) of a cross section perpendicular to the fiber direction of each chopped carbon fiber bundle, namely Dmax/Dmin is from 6.0 to 18.0 (inclusive); and the orientation parameter of the single fibers present in the surface of each chopped carbon fiber bundle is 4.0 or less.

摘要翻译： 提供：具有高流动性而不降低碳纤维的分散性和模制产品的物理性能的短切碳纤维束; 以及生产率高的短切碳纤维束的制造方法。 剪切碳纤维束，其中每根碳纤维束含有总纤度为25,000分特至45,000分特（含）的碳纤维束和相对于1质量％至5质量％（以上）的量的施胶剂 切碎的碳纤维束的总质量。 切断碳纤维束沿着碳纤维束的纤维方向的长度（L）为1mm〜50mm（以下）。 与切断的碳纤维束的纤维方向垂直的截面的最长直径（Dmax）与最短直径（Dmin）的比率为6.0〜18.0（以下）。 并且每个切碎的碳纤维束的表面中存在的单纤维的取向参数为4.0以下。