    STAINLESS STEEL RESISTANT TO DELAYED CRACKING AND A METHOD FOR ITS PRODUCTION
    2.
    发明公开
    STAINLESS STEEL RESISTANT TO DELAYED CRACKING AND A METHOD FOR ITS PRODUCTION 审中-公开
    与抗病性的FOR延迟裂纹和方法不锈钢ITS

    公开(公告)号：EP3017072A1

    公开(公告)日：2016-05-11

    申请号：EP14820539.6

    申请日：2014-06-19

    申请人： Outokumpu Oyj

    发明人： TALONEN, Juho

    IPC分类号： C21D3/06 ,  C21D3/00 ,  C21D8/00 ,  C21D7/02 ,  C21D8/02 ,  C22C38/40

    CPC分类号： C21D3/06 ,  C21D1/74 ,  C21D6/001 ,  C21D6/002 ,  C21D6/005 ,  C21D8/0436 ,  C22C38/001 ,  C22C38/02 ,  C22C38/40 ,  C22C38/42 ,  C22C38/58

    摘要： The invention relates to a stainless steel exhibiting transformation-induced plasticity (TRIP) effect resistant to delayed cracking and to the method for producing the stainless steel. The resistance to delayed cracking in the stainless steel is achieved limiting the total hydrogen content of the stainless steel measured by inert gas fusion method below 4 weight ppm, preferably below 3 weight ppm by a heat treatment performed at the temperature range between 100° C. and 700° C. for 0.1-300 hours, preferably at 200-600° C. for 1-100 hours, and more preferably at 250-500° C. for 1-100 hours.

    摘要翻译： 本发明涉及到一个不锈钢参展变诱发塑性（TRIP）效应的延迟开裂以及一种用于制造不锈钢的方法具有抗性。 延迟电阻在不锈钢裂化是通过在温度范围100℃之间进行热处理取得限制由惰性气体熔融法低于4重量ppm的测量的不锈钢的总氢含量，优选低于3重量ppm的 和700℃下进行0.1-300小时，优选在200〜600℃下进行1〜100小时，更优选在250-500℃下1-100小时。

    HIGH STRENGTH AUSTENITIC STAINLESS STEEL AND PRODUCTION METHOD THEREOF
    4.
    发明公开
    HIGH STRENGTH AUSTENITIC STAINLESS STEEL AND PRODUCTION METHOD THEREOF 审中-公开
    高强度奥氏体不锈钢及其生产方法

    公开(公告)号：EP3191612A1

    公开(公告)日：2017-07-19

    申请号：EP15834538.9

    申请日：2015-08-21

    申请人： Outokumpu Oyj

    发明人： TALONEN, Juho

    IPC分类号： C22C38/48 ,  C22C38/50 ,  C22C38/46 ,  C22C38/44 ,  C22C38/42 ,  C22C38/58 ,  C21D8/02 ,  C21D1/26

    CPC分类号： C21D9/46 ,  C21D1/26 ,  C21D8/0236 ,  C21D8/0273 ,  C21D2211/001 ,  C22C38/001 ,  C22C38/002 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/46 ,  C22C38/48 ,  C22C38/50 ,  C22C38/58

    摘要： An austenitic stainless steel including in weight % 0-0.4% C, 0-3% Si, 3-20% Mn, 10-30% Cr, 0-4.5% Ni, 0-3% Mo, 0-3% Cu, 0.05-0.5% N, 0-0.5% Nb, 0-0.5% Ti, 0-0.5% V, the balance of Fe and inevitable impurities. The content of at least one of the elements in the group of niobium (Nb), titanium (Ti) or vanadium (V) is more than 0.05% so that the total amount of niobium (Nb), titanium (Ti) and vanadium (V) contents is in the range of 0.05-0.5%. The grain size of the steel is less than 10 micrometer after annealing the cold deformed product and the difference between the yield strengths of the steel measured in transverse and parallel directions to the rolling direction is lower than 5%. Also, a method for producing the austenitic stainless steel.

    摘要翻译： 本发明涉及一种奥氏体不锈钢。 钢中含有0-0.4％C，0-3％Si，3-20％Mn，10-30％Cr，0-4.5％Ni，0-3％Mo，0-3％Cu， 0.5％N，0-0.5％Nb，0-0.5％Ti，0-0.5％V，其余为Fe和不可避免的杂质。 铌（Nb），钛（Ti）或钒（V）中至少一种元素的含量大于0.05％，使得铌（Nb），钛（Ti）和钒 （V）的含量在冷变形产品退火后具有小于10微米的晶粒尺寸以及在横向和平行方向上测量的钢的屈服强度与轧制方向之间的差异的范围为0.05-0.5％ 低于5％。 本发明还涉及生产这种奥氏体不锈钢的方法。

    LOW-NICKEL AUSTENITIC STAINLESS STEEL AND USE OF THE STEEL
    6.
    发明公开
    LOW-NICKEL AUSTENITIC STAINLESS STEEL AND USE OF THE STEEL 审中-公开
    AUSTENITISCHER EDELSTAHL MIT GERINGEM NICKELANTEIL UND VERWENDUNG DIESES STAHLS

    公开(公告)号：EP2566994A1

    公开(公告)日：2013-03-13

    申请号：EP11777324.2

    申请日：2011-04-18

    申请人： Outokumpu Oyj

    发明人： TALONEN, Juho ,  TAULAVUORI, Tero ,  KODUKULA, Suresh

    IPC分类号： C22C38/58 ,  C22C38/54 ,  C22C38/50 ,  C22C38/48 ,  C22C38/46 ,  C22C38/44 ,  C22C38/42 ,  C22C38/40 ,  C21C5/00

    CPC分类号： C22C38/58 ,  C21D6/002 ,  C21D6/005 ,  C22C38/001 ,  C22C38/02 ,  C22C38/42

    摘要： The invention relates to a low-nickel austenitic stainless steel with high resistance to delayed cracking and the use of the steel. The steel contains in weight % 0,02 - 0,15 % carbon, 7 - 15 % manganese, 14 - 19 % chromium, 0,1 - 4 % nickel, 0,1 - 3 % copper, 0,05 - 0,3 % nitrogen, the balance of the steel being iron and inevitable impurities, and the chemical composition range in terms of the sum of carbon and nitrogen contents (C+N) and the measured Md3o-temperature is inside the area defined by the points ABCD which have the following values Point M
    d30 °C C+N % A - 80 0,1 B + 7 0,1 C - 40 0,40 D - 80 0,40.

    摘要翻译： 本发明涉及一种具有高耐延迟开裂性和低使用性的低镍奥氏体不锈钢。 钢含有重量百分比为0.02-0.15％碳，7-15％锰，14-19％铬，0.1-4％镍，0.1-3％铜，0.05-0.3％氮，余量为铁和 不可避免的杂质，碳和氮含量（C + N）和测量的Md3o温度之和的化学成分范围在由具有以下值的点ABCD定义的区域内的点Md30℃C + N％A-80 0.1 B + 7 0.1 C-40 0.40 D-80 0.40。